Experimental Insights into Mesoporous Polyaniline-Based Nanocomposites for Anionic and Cationic Dye Removal.

This work presents the preparation of inorganic-organic hybrid nanocomposites, namely three-dimensional polyaniline (Pani)/activated silica gel (ASG) (3D Pani@ASG), their characterization, and in removing application as a potential adsorbent for cationic brilliant green (BG), crystal violet (CV), and anionic Congo red (CR), and methyl orange (MO) dyes. Pani@ASG nanocomposites have been prepared by the in situ polymerization method and characterized using various techniques such as Fourier transform infrared (FTIR), X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM) with selected area electron diffraction, thermogravimetric analysis with derivative thermogravimetry, zeta potential analyses, and Brunauer-Emmett-Teller (BET). The scanning electron microscopy (SEM) study confirms the average particle size of the Pani@ASG nanocomposite is in the range of 5 nm. FESEM, TEM, FTIR, and XRD analysis proved the successful decoration of ASG over Pani. The BET result of Pani@ASG shows a mesoporous nature with a pore diameter of less than 3 nm and a surface area of 423.90 m2 g-1. Both SEM and TEM analyses show the proportional distribution of ASG over Pani's surface. The adsorption trend of BG and MO on the studied materials at pH 7 was found as follows: Pani@ASG > Pani > ASG. The highest sorption capacities of MO and BG on Pani@ASG were 161.29 and 136.98 mg/g (T = 298.15 K, and Pani@ASG dose: 0.04 g for MO and 0.06 g for BG), which were greater compared with bare Pani and bare ASG, respectively. The interaction mechanism behind the adsorption of BG and MO dyes onto the Pani@ASG nanocomposite includes electrostatic interaction, π-π interaction, and hydrogen bonding. The mechanistic pathway and the interactions between the targeted dyes and Pani@ASG were further studied using adsorption isotherm, adsorption kinetics, and thermodynamics.