Correction: Weingart et al. Expanded Polycarbonate (EPC)-A New Generation of High-Temperature Engineering Bead Foams. Polymers 2020, 12, 2314.

In the original publication [...].

Error in Table

In the original publication [1], there was a mistake in the legend for Table 4: Summary of bending characteristic-values of EPC, EPP and EPET at 25, 80 and 110 °C. There is a copy and paste error. In the EPC 110 °C column, the values need to be (top to bottom) 61.0 ± 2.2; 1.4 ± 0.10; 9.5 ± 0.5; 7.7 ± 0.6. The correct legend appears below. The authors apologize for any inconvenience caused and state that the scientific conclusions are unaffected. The original publication has also been updated.

Table 4

Summary of bending characteristic-values of EPC, EPP and EPET at 25, 80 and 110 °C.

		EPC	EPP	EPET
25 °C	Bending-Modulus/MPa	70.5 ± 4.5	45.3 ± 1.6	69.2 ± 6.6
	Bending-Strength/MPa	2.5 ± 0.20	1.60 ± 0.06	1.32 ± 0.05
	Bending Strain at max. F/%	7.7 ± 1.3	9.6 ± 0.7	2.2 ± 0.2
	Elongation at max. F (Tensile)/%	8.4 ± 1.2	20.2 ± 1.1	2.7 ± 0.4
		EPC	EPP	EPET
80 °C	Bending-Modulus/MPa	65.3 ± 3.0	8.3 ± 1.5	23.4 ± 1.5
	Bending-Strength/MPa	1.8 ± 0.12	0.54 ± 0.8	0.90 ± 0.03
	Bending Strain at max. F/%	8.0 ± 1.0	11.0 ± 0.5	5.5 ± 0.8
	Elongation at max. F (Tensile)/%	6.6 ± 0.5	51.0 ± 4.5	3.6 ± 1.1
		EPC	EPP	EPET
110 °C	Bending-Modulus/MPa	61.0 ± 2.2	3.0 ± 0.4	6.4 ± 0.8
	Bending-Strength/MPa	1.4 ± 0.10	0.25 ± 0.02	0.38 ± 0.04
	Bending Strain at max. F/%	9.5 ± 0.5	13.0 ± 0.8	7.6 ± 0.8
	Elongation at max. F (Tensile)/%	7.7 ± 0.6	97.3 ± 18.6	8.4 ± 0.3