Photocatalytic degradation of organic synthetic dyes and textile dyeing waste water by Al and F co-doped TiO2 nanoparticles.

Textile wastewater threatens people health by alluring diseases and revealing public existing close to the waste to the dangerous products within. Because waste causes a risk to the environment and people, waste management making is the main challenge of the municipal world. Environmental process such as toxic dye degradation can be stepped up through photochemical process such as visible light induced catalytic degradation. Here, the successful synthesis of co-doping of Al and F into TiO2 nanoparticles (Al-F∕TiO2 NPs) by solid state reaction method comprising different proportions of co-dopants is evaluated for the applications of degrading organic synthetic dyes and textile dyeing waste water. Influence of co-dopants was studied in their optical, structural, compositional, morphological and vibrational properties. The average crystallite size of Al-F∕TiO2 NPs was found as 15 nm.FTIR and UV-vis spectrum confirmed F and Al atoms were incorporated into the TiO2 lattice.The absorption edges slightly moved to shorter wavelength by increasing level of dopants and this specifies the control of optical absorption of TiO2 by the incorporation of F and Al3+ ions.The EDS spectrum indicates the purity of the samples. The highest zone of inhibition for the prepared nanoparticles over Staphylococcus aureus reached to 22 mm. The rate constant (kapp) value of MB, MO and textile waste water is 0.0138/min, 0.0174/min and 0.0139/min for the prepared nanoparticles respectively. The study of photocatalytic degradation of visible light assisted MB, MO and real textile waste water by Al-F∕TiO2 NPs revealed that the prepared nanoparticles act as ideal catalyst by tuning the concentration of co-dopants in TiO2.