Long Zhang1, Xiaoyu Cao1, Chao Feng2, Weiyi Zhang3, Zhifei Wang1, Sijia Feng1, Zhaodi Huang1, Xiaoqing Lu1, Fangna Dai1. 1. College of Science, School of Materials Science and Engineering, China University of Petroleum (East China), Qingdao, Shandong 266580, P. R. China. 2. State Key Laboratory of Heavy Oil Processing, China University of Petroleum (East China), Qingdao, Shandong 266580, P. R. China. 3. Advanced Materials Institute, Qilu University of Technology, (Shandong Academy of Sciences), Jinan, Shandong 250014, P. R. China.
Abstract
Molybdenum diselenide (MoSe2) has been considered as promising electrocatalysts for catalyzing the hydrogen evolution reaction (HER) due to its narrow band gap and appropriate adsorption free energy. However, its catalytic performance is still impeded by inferior electrical conductivity and insufficient active sites, thus leading to unsatisfactory HER performance. Herein, MoSe2@N-doped carbon (NC) hollow nanoflowers with interfacial Mo-N-C bonds were controllably fabricated through the in situ selenization of the self-polymerized Mo-polydopamine precursor. Benefiting from the unique hollow structure, NC protective layer, and intimate interfacial interaction, the optimal MoSe2@NC displays good HER performance with low overpotentials (175 and 183 mV) and long-term stability (up to 12 h at -10 mA cm-2) in 0.5 M H2SO4 and 1.0 M KOH solutions, respectively. The theoretical results show that Mo-N-C bonds at the interface of MoSe2@NC give rise to relatively low unoccupied eg orbital density of states and ideal H2 adsorption free energy. This work presented here highlights the critical role of interfacial chemical bonds in regulating the electronic structure of nanomaterials and further improving the HER performance.
Molybdenum diselenide (n class="Chemical">MoSe2) has been considered as promising electrocatalysts for catalyzing the hydrogen evolution reaction (HER) due to its narrow band gap and appropriate adsorption free energy. However, its catalytic performance is still impeded by inferior electrical conductivity and insufficient active sites, thus leading to unsatisfactory HER performance. Herein, MoSe2@N-doped carbon (NC) hollow nanoflowers with interfacial Mo-N-C bonds were controllably fabricated through the in situ selenization of the self-polymerized Mo-polydopamine precursor. Benefiting from the unique hollow structure, NC protective layer, and intimate interfacial interaction, the optimal MoSe2@NC displays good HER performance with low overpotentials (175 and 183 mV) and long-term stability (up to 12 h at -10 mA cm-2) in 0.5 M H2SO4 and 1.0 M KOH solutions, respectively. The theoretical results show that Mo-N-C bonds at the interface of MoSe2@NC give rise to relatively low unoccupied eg orbital density of states and ideal H2 adsorption free energy. This work presented here highlights the critical role of interfacial chemical bonds in regulating the electronic structure of nanomaterials and further improving the HER performance.