Investigation of mechanical performances and polymerization shrinkage of dual-cured resin composites as core build-up material.

This study systematically compared the mechanical performances and polymerization shrinkage of two novel dual-cured resin composites (DCRC) with one conventional packable light-cured resin composite (LCRC) for their application as core build-up material by micro-hardness test, flexural strength test, push-out test, and digital image correlation analysis. The LCRC had a significantly higher micro-hardness (p<0.05) whereas the bond strength demonstrated no difference. The mean values of three materials ranged from 35.16 and 64.82 for the Vickers hardness and from 4.66 MPa to 11.53 MPa for the bond strength. The flexure strength of the three materials was not statistically different from each other. LCRC demonstrated 1.88% of volumetric shrinkage while the two DCRC showed 5.06% and 4.91%, respectively. In general, the DCRC demonstrated a comparable flexural strength and bond strength as the LCRC, however, the significant polymerization shrinkage of DCRC should be emphasized.