Effect of Particle Size on the Mechanical Properties of TiO2-Epoxy Nanocomposites.

This study investigated the effects of the packing density and particle size distribution of TiO2 nanoparticles on the mechanical properties of TiO2-epoxy nanocomposites (NCs). The uniform dispersion and good interfacial bonding of TiO2 in the epoxy resin resulted in improved mechanical properties with the addition of nanoparticles. Reinforcement nano-TiO2 particles dispersed in deionized water produced by three different ultrasonic dispersion methods were used; the ultrasonication effects were then compared. The nano-TiO2 suspension was added at 0.5-5.0 wt.%, and the mechanical and thermal properties of TiO2-epoxy NCs were compared using a universal testing machine, scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), and differential scanning calorimetry (DSC). The tensile strength of the NCs was improved by the dispersion strengthening effect of the TiO2 nanoparticles, and focused sonication improved the tensile strength the most when nano-TiO2 suspensions with a particle size of 100 nm or smaller were used. Thus, the reinforcing effect of TiO2 nanoparticles on the epoxy resin was observed, and the nano-TiO2 suspension produced by focused sonication showed a more distinct reinforcing effect.