Ling Zhang1, Yuedan Xu2, Xinyang Jin2, Chaoyang Wang2, Mingxing Li2, Zihuai Zhou2, Baiping Fu3. 1. Department of Prosthodontics, The Affiliated Hospital of Stomatology, School of Stomatology, Zhejiang University School of Medicine, Yan'an Road 395, Hangzhou, Zhejiang 310006, China; Key Laboratory of Oral Biomedical Research of Zhejiang Province, Hangzhou, Zhejiang 310006, China. Electronic address: zl1616-@163.com. 2. Department of Prosthodontics, The Affiliated Hospital of Stomatology, School of Stomatology, Zhejiang University School of Medicine, Yan'an Road 395, Hangzhou, Zhejiang 310006, China; Key Laboratory of Oral Biomedical Research of Zhejiang Province, Hangzhou, Zhejiang 310006, China. 3. Department of Prosthodontics, The Affiliated Hospital of Stomatology, School of Stomatology, Zhejiang University School of Medicine, Yan'an Road 395, Hangzhou, Zhejiang 310006, China; Key Laboratory of Oral Biomedical Research of Zhejiang Province, Hangzhou, Zhejiang 310006, China. Electronic address: fbp@zju.edu.cn.
Abstract
AIMS: To investigate the biomimetic fabrication of fibrous-like organic-inorganic hybrid structures via a simple bottom-up approach, viz. self-assembly of simple molecules, and apply fibrous-like composites as a novel primer to improve dentin bond strengths of self-etch adhesives. MATERIALS AND METHODS: The resultants of commercial amorphous calcium phosphate (ACP) nanoparticles and 10-methacryloyloxydecyl dihydrogen phosphate (MDP) ethanol-aqueous solution were analyzed by TEM, SEM, XRD, DLS and AFM. The acid and alkali resistance of abovementioned self-assembled composites were analyzed with TEM. Micro-tensile bond strengths (MTBS) tests were performed after polished dentin surfaces were pretreated with self-assembled composites. The pretreated dentin surfaces and dentin-resin interfaces were characterized by SEM/TEM. KEY FINDINGS: ACP nanoparticles in MDP solution could self-assemble into fibrous-like nanotube structures in 8 nm diameter. Self-assembly and self-proliferation process went from ACP nanoparticles, dissolved ACP nanoparticles (less than 50 nm), twig-like structures and fibrous-like nanotubes to cellular networks. The fibrous-like nanotubes were only detected when the amount of ACP in reaction system were more than 0.01 g. The more ACP interacted with MDP, the more fibrous-like nanotubes were formed. After the dentin surfaces were treated with fibrous-like nanotube composites, MTBS could be significantly improved. Moreover, the fibrous-like nanotube structures could be resistant to acidic challenge, and were stable at least for 3 months. SIGNIFICANCE: The fibrous-like nanotube structures could be self-assembled via a bottom-up approach at certain ratio of MDP and commercial ACP nanoparticles. The application of fibrous-like nanotube composites as a novel primer prior to self-etch adhesives greatly improved dentin bond strengths.
AIMS: To investigate the biomimetic fabrication of fibrous-like organic-inorganic hybrid structures via a simple bottom-up approach, viz. self-assembly of simple molecules, and apply fibrous-like composites as a novel primer to improve dentin bond strengths of self-etch adhesives. MATERIALS AND METHODS: The resultants of commercial amorphous calcium phosphate (ACP) nanoparticles and 10-methacryloyloxydecyl dihydrogen phosphate (MDP) ethanol-aqueous solution were analyzed by TEM, SEM, XRD, DLS and AFM. The acid and alkali resistance of abovementioned self-assembled composites were analyzed with TEM. Micro-tensile bond strengths (MTBS) tests were performed after polished dentin surfaces were pretreated with self-assembled composites. The pretreated dentin surfaces and dentin-resin interfaces were characterized by SEM/TEM. KEY FINDINGS:ACP nanoparticles in MDP solution could self-assemble into fibrous-like nanotube structures in 8 nm diameter. Self-assembly and self-proliferation process went from ACP nanoparticles, dissolved ACP nanoparticles (less than 50 nm), twig-like structures and fibrous-like nanotubes to cellular networks. The fibrous-like nanotubes were only detected when the amount of ACP in reaction system were more than 0.01 g. The more ACP interacted with MDP, the more fibrous-like nanotubes were formed. After the dentin surfaces were treated with fibrous-like nanotube composites, MTBS could be significantly improved. Moreover, the fibrous-like nanotube structures could be resistant to acidic challenge, and were stable at least for 3 months. SIGNIFICANCE: The fibrous-like nanotube structures could be self-assembled via a bottom-up approach at certain ratio of MDP and commercial ACP nanoparticles. The application of fibrous-like nanotube composites as a novel primer prior to self-etch adhesives greatly improved dentin bond strengths.