Spark Plasma Sintering of Aluminum-Based Powders Reinforced with Carbon Nanotubes: Investigation of Electrical Conductivity and Hardness Properties.

This paper focuses on reporting results obtained by the spark plasma sintering (SPS) consolidation and characterization of aluminum-based nanocomposites reinforced with concentrations of 0.5 wt%, 1 wt% and 2 wt% of single-walled carbon nanotubes (SWCNTs) and multi-walled carbon nanotubes (MWCNTs). Experimental characterization performed by SEM shows uniform carbon nanotube (CNT) dispersion as well as carbon clusters located in the grain boundary of the Al matrix. The structural analysis and crystallite size calculation were performed by X-ray diffraction tests, detecting the characteristic CNT diffraction peak only for the composites reinforced with MWCNTs. Furthermore, a considerable increment in the crystallite size value for those Al samples reinforced and sintered with 1 wt% of CNTs was observed. Hardness tests show an improvement in the composite surface hardness of about 11% and 18% for those samples reinforced with 2 wt% of SWNCTs and MWCNTs, respectively. Conductivity measurements show that the Al samples reinforced with 2 wt% of MWCNTs and with 0.5 wt% SWCNTs reach the highest IACS values of 50% and 34%, respectively.