Synthesis of manganese doped β-FeOOH and MnFe2O4 nanorods for enhanced drug delivery and hyperthermia application.

Preparation of manganese ferrite (MnFe2O4) nanorods by the reduction of akaganeite seeds in the presence of oleylamine is reported. The Mn-doped β-FeOOH akaganeite seeds have been processed by the hydrolysis of metal-chloride salts in the presence of polyethylenimine (PEI) surfactant. The hydrophobic oleylamine capped nanorods are made hydrophilic using trisodium citrate as a phase transferring agent. The nanorods form with an aspect ratio of 5.47 and possess a high magnetisation value of 69 emu/g at an applied magnetic field of 1.5 T. The colloidal water dispersion of nanorods exhibits superior heating efficiency by the application of alternating magnetic field (AMF). A specific absorption rate value of 798 W/g is achieved at an applied AMF of field strength 500 Oe and frequency 316 kHz. Further, the citrate functionalised nanorods are capable of attaching with doxorubicin (DOX) electrostatically with a loading efficiency of 97% and the drug release is pH responsive. The DOX loaded nanorods show a promising effect on the apoptosis of MCF-7 as experimented in vitro.