Laser Powder Bed Fusion of Pure Tungsten: Effects of Process Parameters on Morphology, Densification, Microstructure.

Tungsten has been widely used in many industrial fields due to its excellent properties. However, owing to its characteristics of inherent brittleness at room temperature and high melting point, it is difficult to prepare tungsten parts with high complexity via traditional methods. In the present work, tungsten samples were prepared by laser powder bed fusion. The influence of each process parameter including laser power, scanning speed, and hatch spacing on the surface morphology, densification, and microstructure of tungsten samples was systematically investigated. The results showed that the use of the appropriate parameters, especially high laser power, can effectively improve the surface quality and obtain a dense surface. The tungsten samples with a relative density of 98.31% were obtained with optimized parameter combinations: a laser power of 300 W, scanning speed of 400 mm/s, and hatch spacing of 0.08 mm. Compared with scanning speed and hatch spacing, the laser power had a more obvious influence on the relative density. Additionally, for the grain morphology by microstructure inspection, elongated curved grains gradually transformed into fine straight columnar grains as the scanning speed increased. The hatch spacing would change the grain morphology slightly but had no significant effect on the grain size.