Beatriz Martínez-Sánchez1, Diego Cazorla-Amorós2, Emilia Morallón1. 1. Departamento de Química Física and Instituto Universitario de Materiales de Alicante (IUMA), University of Alicante, Ap. 99, 03080 Alicante, Spain. 2. Departamento de Química Inorgánica and Instituto Universitario de Materiales de Alicante (IUMA), University of Alicante, Ap. 99, 03080 Alicante, Spain.
Abstract
Phosphonated polyanilines were synthesized by copolymerization of aniline (ANI) with both 2- and 4-aminophenylphosphonic acids (APPA). The material composition and the final properties of the copolymers can be easily tailored by controlling the monomers ANI/APPA molar feed ratio. An important influence on the reactivity of monomers has been found with the substituent position in the ring, leading to differences in the properties and size of blocks of each monomer in the polymer. As expected, while 2APPA shows more similarities to ANI, 4APPA is much less reactive. Phosphorus loading of ~5 at% was achieved in the poly(aniline-co-2-aminophenylphosphonic acid) (PANI2APPA) with a 50/50 molar feed ratio. All the resulting copolymers were characterized by different techniques. Experimental results and density functional theory (DFT) computational calculations suggest that the presence of phosphonic groups in the polymeric chain gives rise to inter- and intra-chain interactions, as well as important steric effects, which induce a slight twist in the substituted PANI structure. Therefore, the physicochemical, electrical, and electrochemical properties are modified and can be suitably controlled.
n class="Chemical">Phosphonatedn class="Chemical">polyanilines were synthesized by copolymerization of aniline (ANI) with both 2- and 4-aminophenylphosphonic acids (APPA). The material composition and the final properties of thecopolymers can be easily tailored by controlling the monomers ANI/APPA molar feed ratio. An important influence on the reactivity of monomers has been found with the substituent position in the ring, leading to differences in the properties and size of blocks of each monomer in thepolymer. As expected, while 2APPA shows more similarities to ANI, 4APPA is much less reactive. Phosphorus loading of ~5 at% was achieved in thepoly(aniline-co-2-aminophenylphosphonic acid) (PANI2APPA) with a 50/50 molar feed ratio. All the resulting copolymers were characterized by different techniques. Experimental results and density functional theory (DFT) computational calculations suggest that the presence of phosphonic groups in thepolymeric chain gives rise to inter- and intra-chain interactions, as well as important steric effects, which induce a slight twist in the substituted PANI structure. Therefore, the physicochemical, electrical, and electrochemical properties are modified and can be suitably controlled.