Maciej Gawlikowski1,2, Miroslawa El Fray3, Karolina Janiczak2, Barbara Zawidlak-Węgrzyńska2, Roman Kustosz2. 1. Faculty of Biomedical Engineering, Department of Biosensors and Processing of Biomedical Signals, Silesian University of Technology, Roosevelta 40, 41-800 Zabrze, Poland. 2. Foundation of Cardiac Surgery Development, Artificial Heart Laboratory, Wolności 345a, 41-800 Zabrze, Poland. 3. Faculty of Chemical Technology and Engineering, Department of Polymer and Biomaterials Science, West Pomeranian University of Technology, Al. Piastów 45, 71-311 Szczecin, Poland.
Abstract
(1) Background: The evaluation of ventricular assist devices requires the usage of biocompatible and chemically stable materials. The commonly used polyurethanes are characterized by versatile properties making them well suited for heart prostheses applications, but simultaneously they show low stability in biological environments. (2) Methods: An innovative material-copolymer of poly(ethylene-terephthalate) and dimer linoleic acid-with controlled and reproducible physico-mechanical and biological properties was developed for medical applications. Biocompatibility (cytotoxicity, surface thrombogenicity, hemolysis, and biodegradation) were evaluated. All results were compared to medical grade polyurethane currently used in the extracorporeal heart prostheses. (3) Results: No cytotoxicity was observed and no significant decrease of cells density as well as no cells growth reduction was noticed. Thrombogenicity analysis showed that the investigated copolymers have the thrombogenicity potential similar to medical grade polyurethane. No hemolysis was observed (the hemolytic index was under 2% according to ASTM 756-00 standard). These new materials revealed excellent chemical stability in simulated body fluid during 180 days aging. (4) Conclusions: The biodegradation analysis showed no changes in chemical structure, molecular weight distribution, good thermal stability, and no changes in surface morphology. Investigated copolymers revealed excellent biocompatibility and great potential as materials for blood contacting devices.
(1) Background: The evaluation of ventricular assist devices requires the usage of biocompatible and chemically stable materials. The commonly used polyurethanes are characterized by versatile properties making them well suited for heart prostheses applications, but simultaneously they show low stability in biological environments. (2) Methods: An innovative material-copolymer of poly(ethylene-terephthalate) and dimer linoleic acid-with controlled and reproducible physico-mechanical and biological properties was developed for medical applications. Biocompatibility (cytotoxicity, surface thrombogenicity, hemolysis, and biodegradation) were evaluated. All results were compared to medical grade polyurethane currently used in the extracorporeal heart prostheses. (3) Results: No cytotoxicity was observed and no significant decrease of cells density as well as no cells growth reduction was noticed. Thrombogenicity analysis showed that the investigated copolymers have the thrombogenicity potential similar to medical grade polyurethane. No hemolysis was observed (the hemolytic index was under 2% according to ASTM 756-00 standard). These new materials revealed excellent chemical stability in simulated body fluid during 180 days aging. (4) Conclusions: The biodegradation analysis showed no changes in chemical structure, molecular weight distribution, good thermal stability, and no changes in surface morphology. Investigated copolymers revealed excellent biocompatibility and great potential as materials for blood contacting devices.