Preparation of stretchable composite film and its application in skin burn repair.

The poor elasticity of wound dressings often leads to wound healing failure due to rupture and fall off. In this study, the composite films of zein and hydrogel poly (acrylic acid) were developed in order to obtain stretchable wound dressing for skin burn repair. The mechanical test revealed that the maximum elongation of break of composite films could reach 349.76% when the mass ratio of zein to poly (acrylic acid) was 1.5. SEM and FTIR analysis demonstrated the good elasticity of composite films might be due to the formation of a dense structure and the strong interaction between zein and poly (acrylic acid). Interestingly, the composite films exhibited great adhesiveness to human finger skin and stretchable ability under strenuous joint exercise. CCK-8 assay and fluorescence staining showed that the composite films and their extract had good cytocompatibility on human foreskin fibroblasts (L929) cells. The in vivo experiment on rat's skin burning model indicated that the composite films could promote wound healing and collagen synthesis by comparison with commercial gauze. It could be concluded that the stretchable composite films of zein and hydrogel poly (acrylic acid) had the potential as the wound dressing.