Preparation and Characterization of Zinc Hydroxystannate Coated by Aluminum Phosphate and Its Application in Poly(acrylonitrile-co-vinylidene chloride).

In this study, zinc hydroxystannate ([ZnSn(OH)6], ZHS) was coated with aluminum phosphate (AlPO4, ALP) to prepare the ZHS-ALP composite. During the coating process, the reaction conditions, such as the ALP to ZHS molar ratio, were controlled, and the morphology of the products was characterized by scanning electron microscopy (SEM). The prepared composites were introduced into poly(acrylonitrile-co-vinylidene chloride) (PANVDC), and the change in compatibility between ZHS and the polymer matrix was characterized. The results showed that ALP-ZHS (1:1), which was prepared by ALP-ZHS composite molar ratio of 1:1, could improve the dispersion and compatibility of ZHS in the polymer matrix and decrease the hydrophilicity and viscosity. Moreover, the ALP-ZHS composite had a better flame-retardant effect on PANVDC than ZHS alone. PANVDC could pass the V-0 rating in UL94, particularly the highest limiting oxygen index (LOI) value of 33.2% obtained when the ALP-ZHS (1:1) composite was added to PANVDC.