OBJECTIVE: Micro-fabricated neural interfaces based on polyimide (PI) are achieving increasing importance in translational research. The ability to produce well-defined micro-structures with properties that include chemical inertness, mechanical flexibility and low water uptake are key advantages for these devices. APPROACH: This paper reports the development of the transverse intrafascicular multichannel electrode (TIME) used to deliver intraneural sensory feedback to an upper-limb amputee in combination with a sensorized hand prosthesis. A failure mode analysis on the explanted devices was performed after a first-in-human study limited to 30 d. MAIN RESULTS: About 90% of the stimulation contact sites of the TIMEs maintained electrical functionality and stability during the full implant period. However, optical analysis post-explantation revealed that 62.5% of the stimulation contacts showed signs of delamination at the metallization-PI interface. Such damage likely occurred due to handling during explantation and subsequent analysis, since a significant change in impedance was not observed in vivo. Nevertheless, whereas device integrity is mandatory for long-term functionality in chronic implantation, measures to increase the bonding strength of the metallization-PI interface deserve further investigation. We report here that silicon carbide (SiC) is an effective adhesion-promoting layer resisting heavy electrical stimulation conditions within a rodent animal trial. Optical analysis of the new electrodes revealed that the metallization remained unaltered after delivering over 14 million pulses in vivo without signs of delamination at the metallization-PI interface. SIGNIFICANCE: Failure mode analysis guided implant stability optimization. Reliable adhesion of thin-film metallization to substrate has been proven using SiC, improving the potential transfer of micro-fabricated neural electrodes for chronic clinical applications. (Document number of Ethical Committee: P/905/CE/2012; Date of approval: 2012-10-04).
OBJECTIVE: Micro-fabricated neural interfaces based on polyimide (PI) are achieving increasing importance in translational research. The ability to produce well-defined micro-structures with properties that include chemical inertness, mechanical flexibility and low water uptake are key advantages for these devices. APPROACH: This paper reports the development of the transverse intrafascicular multichannel electrode (TIME) used to deliver intraneural sensory feedback to an upper-limb amputee in combination with a sensorized hand prosthesis. A failure mode analysis on the explanted devices was performed after a first-in-human study limited to 30 d. MAIN RESULTS: About 90% of the stimulation contact sites of the TIMEs maintained electrical functionality and stability during the full implant period. However, optical analysis post-explantation revealed that 62.5% of the stimulation contacts showed signs of delamination at the metallization-PI interface. Such damage likely occurred due to handling during explantation and subsequent analysis, since a significant change in impedance was not observed in vivo. Nevertheless, whereas device integrity is mandatory for long-term functionality in chronic implantation, measures to increase the bonding strength of the metallization-PI interface deserve further investigation. We report here that silicon carbide (SiC) is an effective adhesion-promoting layer resisting heavy electrical stimulation conditions within a rodent animal trial. Optical analysis of the new electrodes revealed that the metallization remained unaltered after delivering over 14 million pulses in vivo without signs of delamination at the metallization-PI interface. SIGNIFICANCE: Failure mode analysis guided implant stability optimization. Reliable adhesion of thin-film metallization to substrate has been proven using SiC, improving the potential transfer of micro-fabricated neural electrodes for chronic clinical applications. (Document number of Ethical Committee: P/905/CE/2012; Date of approval: 2012-10-04).
Authors: Kunal Sahasrabuddhe; Aamir A Khan; Aditya P Singh; Tyler M Stern; Yeena Ng; Aleksandar Tadić; Peter Orel; Chris LaReau; Daniel Pouzzner; Kurtis Nishimura; Kevin M Boergens; Sashank Shivakumar; Matthew S Hopper; Bryan Kerr; Mina-Elraheb S Hanna; Robert J Edgington; Ingrid McNamara; Devin Fell; Peng Gao; Amir Babaie-Fishani; Sampsa Veijalainen; Alexander V Klekachev; Alison M Stuckey; Bert Luyssaert; Takashi D Y Kozai; Chong Xie; Vikash Gilja; Bart Dierickx; Yifan Kong; Malgorzata Straka; Harbaljit S Sohal; Matthew R Angle Journal: J Neural Eng Date: 2021-02-24 Impact factor: 5.379
Authors: Dario Farina; Ivan Vujaklija; Rickard Brånemark; Anthony M J Bull; Hans Dietl; Bernhard Graimann; Levi J Hargrove; Klaus-Peter Hoffmann; He Helen Huang; Thorvaldur Ingvarsson; Hilmar Bragi Janusson; Kristleifur Kristjánsson; Todd Kuiken; Silvestro Micera; Thomas Stieglitz; Agnes Sturma; Dustin Tyler; Richard F Ff Weir; Oskar C Aszmann Journal: Nat Biomed Eng Date: 2021-05-31 Impact factor: 25.671
Authors: Bruce Harland; Zaid Aqrawe; Maria Vomero; Christian Boehler; Ernest Cheah; Brad Raos; Maria Asplund; Simon J O'Carroll; Darren Svirskis Journal: Adv Sci (Weinh) Date: 2022-05-02 Impact factor: 17.521