Nina Lümkemann1, Regina Pfefferle1, Eva Jerman1, Beatrice Sener2, Bogna Stawarczyk3. 1. Department of Prosthetic Dentistry, University Hospital, LMU Munich, Goethestrasse 70, 80336 Munich, Germany. 2. Periodontics and Cardiology, Clinic for Preventive Dentistry, University of Zurich, Plattenstrasse 11, 8032 Zurich, Switzerland. 3. Department of Prosthetic Dentistry, University Hospital, LMU Munich, Goethestrasse 70, 80336 Munich, Germany. Electronic address: bogna.stawarczyk@med.uni-muenchen.de.
Abstract
OBJECTIVE: This investigation tested pre-shaded 3Y-TZP materials on optical, mechanical and structural properties and calculated correlations between these properties. METHODS: Seven A2-shaded 3Y-TZP zirconia materials were investigated on translucency (T) via UV-vis-spectrophotometer, fracture load of 3-unit FDPs (FL), biaxial flexural strength (FS), Chevron-Notch Beam (CNB), fracture toughness (KIC) and Martens parameter (hardness: HM and indentation modulus: EIT). FL, FS and KIC were measured in a universal testing machine. The grain size was evaluated by scanning electron microscopy (SEM). Data was analyzed using one-way ANOVA followed by post hoc Scheffé, Kruskal-Wallis-, Mann-Whitney-U- and Pearson-test (p<0.05). RESULTS: For translucency, negative correlations were found with results of facture load (R=-0.444, p<0.001) and KIC (R=-0.503, p<0.001). While a positive correlation was found between translucency and flexural strength (R=0.238, p=0.019), between fracture load and EIT (R=0.227, p<0.029), between fracture load and KIC (R=0.362, p<0.001) as well as between fracture load and the grain size (R=0.598, p=0.007). While the grain size positively correlated with EIT (R=0.534, p=0.017) as well as EIT with HM (R=0.720, p<0.001). SIGNIFICANCE: Despite of being based on the same raw material, tested zirconia materials significantly differed regarding optical, mechanical (except biaxial flexural strength and Martens hardness) and structural properties. Materials with highest optical properties were those with lowest mechanical properties (CER, COP).
OBJECTIVE: This investigation tested pre-shaded 3Y-TZP materials on optical, mechanical and structural properties and calculated correlations between these properties. METHODS: Seven A2-shaded 3Y-TZP zirconia materials were investigated on translucency (T) via UV-vis-spectrophotometer, fracture load of 3-unit FDPs (FL), biaxial flexural strength (FS), Chevron-Notch Beam (CNB), fracture toughness (KIC) and Martens parameter (hardness: HM and indentation modulus: EIT). FL, FS and KIC were measured in a universal testing machine. The grain size was evaluated by scanning electron microscopy (SEM). Data was analyzed using one-way ANOVA followed by post hoc Scheffé, Kruskal-Wallis-, Mann-Whitney-U- and Pearson-test (p<0.05). RESULTS: For translucency, negative correlations were found with results of facture load (R=-0.444, p<0.001) and KIC (R=-0.503, p<0.001). While a positive correlation was found between translucency and flexural strength (R=0.238, p=0.019), between fracture load and EIT (R=0.227, p<0.029), between fracture load and KIC (R=0.362, p<0.001) as well as between fracture load and the grain size (R=0.598, p=0.007). While the grain size positively correlated with EIT (R=0.534, p=0.017) as well as EIT with HM (R=0.720, p<0.001). SIGNIFICANCE: Despite of being based on the same raw material, tested zirconia materials significantly differed regarding optical, mechanical (except biaxial flexural strength and Martens hardness) and structural properties. Materials with highest optical properties were those with lowest mechanical properties (CER, COP).
Authors: Christie M Tafur-Zelada; Oscar Carvalho; Filipe S Silva; Bruno Henriques; Mutlu Özcan; Júlio C M Souza Journal: Clin Oral Investig Date: 2021-03-30 Impact factor: 3.573