Quantitative Determination of the Vertical Segregation and Molecular Ordering of PBDB-T/ITIC Blend Films with Solvent Additives.

The vertical component distribution of bulk heterojunction (BHJ) active film shows a significant impact on determining the device performance in polymer solar cells (PSCs). Processing solvent additives are well known for regulating the BHJ active layer morphology; however, there are few reports regarding the quantitative evaluation of the effect. Herein, a study of the quantitative determination of the vertical segregation in combination of molecular ordering of PBDB-T/ITIC blend films with various 1,8-diiodooctane (DIO) contents is provided. A 0.5% (volume ratio) DIO-added blend film achieves the highest power conversion efficiency of 10.75%. The reduced performance of the PSCs resulted from the excessive vertical component segregation and overcrystallization investigated by various techniques. X-ray photoelectron spectroscopy indicates that DIO aggravates the PBDB-T enrichment region at the air side. Neutron reflectivity further quantitatively figures out the phase separation effect. Although increased crystallinity of ITIC and a higher face-on ratio of PBDB-T in active layer were obtained with increased DIO content approved by grazing-incidence wide-angle X-ray scattering (GIWAXS), the enhanced vertical distribution along with the enhanced crystal size of ITIC leads to the reduced performance of the PSCs due to the reduced carrier transportation paths between donor and acceptor.