Highly efficient adsorptive removal of sulfamethoxazole from aqueous solutions by porphyrinic MOF-525 and MOF-545.

The metal-organic frameworks MOF-525 and MOF-545 comprised of Zr-oxide clusters and porphyrin moieties in different geometries were synthesized solvothermally and applied for the adsorptive removal of the broadly used organic contaminant sulfamethoxazole (SMX) from water. Both MOFs were found highly efficient for the adsorption of SMX with the maximum adsorption capacities of 585 and 690 mg/g for MOF-525 and MOF-545, respectively. The latter value is the highest adsorption capacity reported so far for the adsorption of SMX molecules on any adsorbent. The adsorption equilibrium could be modeled successfully by the Langmuir model, which showed close to matching with the experimental data. Their adsorption equilibriums were attained within 120 and 30 min for MOF-525 and MOF-545, respectively. MOF-545 with mesopores demonstrated superior adsorption kinetics to MOF-525 with micropores, and the simulation by the pseudo-second-order kinetic model indicated ca. 20 times faster adsorption by MOF-545 than MOF-525. Both showed pH-dependent adsorption of SMX with a gradual reduction at high pH due to the repulsion between negatively charged adsorbent and SMX. The adsorption of SMX conducted over a group of representative MOFs with different physicochemical properties and detailed characterization confirmed that the high adsorption capacity of the porphyrin MOFs is achieved by H-bonding between the SMX molecule and the N-sites of the porphyrin units in the MOFs, π-π interaction, and the high surface area. The adsorbents were easily regenerated by simple washing with acetone and reusable with >95% efficiency during 4 repeated adsorption-desorption cycles.