Microstructure, mechanical properties, and degradation of Mg-Ag alloy after equal-channel angular pressing.

Enhancing the strength of Mg-based biodegradable alloys without decreasing their corrosion resistance is a major engineering challenge. In addition, the growing demand for effective reduction of infections and inflammation after implant placement motivates the design of alloys with appropriate compositions or coatings. One promising alloying element is silver, whose antibacterial effect has long been known. Therefore, a Mg-4% Ag alloy was selected for this study. The alloy was investigated under three conditions: as-cast, after T4 treatment, and after T4 treatment with subsequent equal-channel angular pressing (ECAP) using a newly developed double-ECAP die, which offers an equivalent strain per pass of 1.6. The first pass through the double-ECAP die was conducted at 370 °C and the second at 330 °C using route BC. The microstructure of the as-cast Mg-4% Ag consisted of large grains (several hundred microns) and a dendritic structure with micron-sized Mg54Ag17 precipitates. T4 heat treatment caused dissolution of the dendrites and formation of a solid solution without changing the grain size. Consequently, the ultimate compressive strength (UCS) was increased by approximately 30%, and the compressive strain at fracture reached approximately 23%. The compressive yield strength (CYS) remained nearly constant at approximately 30 MPa. Subsequent ECAP led to strong grain refinement (from 350 μm to 38 μm after one pass and 15 μm after two passes) and further increases in the CYS and UCS, to 45 and 300 MPa after the first pass and 62 and 325 MPa after the second pass, respectively. The as-cast alloy exhibited a very high degradation rate in a simulated body fluid at approximately 36 °C. The degradation rate of the alloy after T4 treatment was much lower. Subsequent ECAP had no significant effect on the degradation properties. Thus, it can be concluded that grain refinement has little effect on the degradation rate.