Xuejun Cui1, Lichun Ma2, Guangshun Wu1. 1. School of Chemistry and Materials Science, Ludong University, Yantai 264025, China. 2. Institute of Polymer Materials, Qingdao University, Qingdao 266071, China.
Abstract
A novel and effective strategy was first proposed for the codeposition of a mussel-inspired nanohybrid coating with excellent wettability onto the surface of carbon fibers (CFs) by simultaneous polymerization of bioinspired dopamine (DA) and hydrolysis of commercial tetraethoxysilane (TEOS) in an eco-friendly one-pot process. Mussel-inspired nanohybrids could be adhered onto the surface of CFs firmly. The novel modification could afford sufficient polar groups and significantly improve fiber surface roughness and energy without decreasing fiber intrinsic strength, which were advantageous to promote interfacial compatibility and wettability between CFs and matrix resin. As a result, the interfacial shear strength of composites increased to 48.21 ± 1.45 MPa compared to that of untreated composites 29.47 ± 0.88 MPa. Meanwhile, the nanohybrid coating increased significantly composites' hydrothermal aging resistance. The efficient strategy shows a promising and green platform of surface functionalization of CFs for preparing advanced polymer composites arising from broadly mechanical-demanding and energy-saving usages.
A novel and effective strategy was first proposed for the codeposition of a mussel-inspired nanohybrid coating with excellent wettability onto the surface of n class="Chemical">carbon fibers (CFs) by simultaneous polymerization of bioinspired dopamine (DA) and hydrolysis of commercial tetraethoxysilane (TEOS) in an eco-friendly one-pot process. Mussel-inspired nanohybrids could be adhered onto the surface of CFs firmly. The novel modification could afford sufficient polar groups and significantly improve fiber surface roughness and energy without decreasing fiber intrinsic strength, which were advantageous to promote interfacial compatibility and wettability between CFs and matrix resin. As a result, the interfacial shear strength of composites increased to 48.21 ± 1.45 MPa compared to that of untreated composites 29.47 ± 0.88 MPa. Meanwhile, the nanohybrid coating increased significantly composites' hydrothermal aging resistance. The efficient strategy shows a promising and green platform of surface functionalization of CFs for preparing advanced polymer composites arising from broadly mechanical-demanding and energy-saving usages.