Wen-Yao Huang1, Mei-Ying Chang1, Yen-Zen Wang2, Yu-Chang Huang3, Ko-Shan Ho3, Tar-Hwa Hsieh3, Yu-Chun Kuo3. 1. Department of Photonics, National Sun Yat-sen University, 70 Lienhai Rd., Kaohsiung 80424, Taiwan. 2. Department of Chemical and Materials Engineering, National Yun-Lin University of Science and Technology, 123 University Road, Section 3,Douliou, Yunlin 64002, Taiwan. 3. Department of Chemical and Materials Engineering, National Kaohsiung University of Science & Technology, 415 Chien-Kuo Road, Kaohsiung 80782, Taiwan.
Abstract
Calcination reduction reaction is used to prepare Pt/EB (emeraldine base)-XC72 (Vulcan carbon black) composites as the cathode material of a proton exchange membrane fuel cell (PEMFC). The EB-XC72 core-shell composite obtained from directly polymerizing aniline on XC72 particles is able to chelate and capture the Pt-ions before calcination. X-ray diffraction spectra demonstrate Pt particles are successfully obtained on the EB-XC72 when the calcined temperature is higher than 600 °C. Micrographs of TEM and SEM illustrate the affluent, Pt nanoparticles are uniformly distributed on EB-XC72 at 800 °C (Pt/EB-XC72/800). More Pt is deposited on Pt/EB-XC72 composite as temperatures are higher than 600 °C. The Pt/EB-XC72/800 catalyst demonstrates typical type of a cyclic voltammograms (C-V) curve of a Pt-catalyst with clear Pt-H oxidation and Pt-O reduction peaks. The highest number of transferred electrons during ORR approaches 3.88 for Pt/EB-XC72/800. The maximum power density of the single cell based on Pt/EB-XC72/800 reaches 550 mW cm-2.
Calcination reduction reaction is used to prepare Pt/n class="Chemical">EB (emeraldine base)-XC72 (Vulcan carbon black) composites as the cathode material of a proton exchange membrane fuel cell (PEMFC). The EB-XC72 core-shell composite obtained from directly polymerizing aniline on XC72 particles is able to chelate and capture the Pt-ions before calcination. X-ray diffraction spectra demonstrate Pt particles are successfully obtained on the EB-XC72 when the calcined temperature is higher than 600 °C. Micrographs of TEM and SEM illustrate the affluent, Pt nanoparticles are uniformly distributed on EB-XC72 at 800 °C (Pt/EB-XC72/800). More Pt is deposited on Pt/EB-XC72 composite as temperatures are higher than 600 °C. The Pt/EB-XC72/800 catalyst demonstrates typical type of a cyclic voltammograms (C-V) curve of a Pt-catalyst with clear Pt-H oxidation and Pt-O reduction peaks. The highest number of transferred electrons during ORR approaches 3.88 for Pt/EB-XC72/800. The maximum power density of the single cell based on Pt/EB-XC72/800 reaches 550 mW cm-2.