Synthesis and characterization of magnesium oxide nanoparticle-containing biochar composites for efficient phosphorus removal from aqueous solution.

The effective removal and recovery of phosphorus from aquatic environments are highly important for successful eutrophication control and phosphorus recycling. Herein, we prepared biochar containing MgO nanoparticles (MgO-biochar) by fast pyrolysis of MgCl2-impregnated corn stalks, probed its phosphate adsorption performance. Through the fast pyrolysis, the MgCl2 promoted the formation of micropores and mesoporous, and decomposed into MgO nanoparticles with the size smaller than 100 nm. The adsorption experiments showed that the adsorption property increased with the increase of Mg content, and had a strong correlation with the external surface area. And the phosphate adsorption was well described by the Langmuir-Freundlich model (maximum adsorption capacity was determined as 60.95 mg P/g). Kinetic analysis and characterization analysis of MgO-biochar for different adsorption time indicated that phosphate adsorption onto MgO-biochar was mainly controlled by rapid binding to the external surface (about 75% of the equilibrium adsorption amount), and the uptake rate was limited by the slow diffusion of phosphate into the biochar interior (about 25% of the equilibrium adsorption amount). The results suggested that the synthesized MgO-biochar with enough MgO active site dispersed on a higher external surface can be used as a potential adsorbent for phosphate removal and recovery from aqueous solution.