Hao-Yan Liu1, Zhi-Qiang Zheng2, Cheng Peng3, Jie Lin2. 1. School of Stomatology, Tianjin Medical University, Tianjin 300070, China. 2. Dept. of VIP Dental Service, School and Hospital of Stomatology, Fujian Medical University, Fuzhou 350002, China. 3. Dept. of Stomatology, The Second Hospital of Tianjin Medical University, Tianjin 300201, China.
Abstract
OBJECTIVE: To study the effects of universal adhesives and resin cement on the shear bond strength and durability of zirconia ceramics. METHODS: Zirconia ceramics were sintered into 20 mm×10 mm×10 mm and 10 mm×10 mm×10 mm specimens. The experiment was divided into 12 groups. The two types of specimens were bonded using two variants of resin cement (RelyX Ultimate and Clearfil SAC self-adhesive resin cement), universal adhesives (non-adhesive, Scotchbond uni-versal adhesive, and Clearfil SE One adhesive), and storage conditions (water bath and water bath-thermal cycling). The shear bond strengths were tested, and the fracture morphologies were analyzed. RESULTS: The cement (F=8.41, P<0.01) and adhesive (F=30.34, P<0.01) exerted a significant effect on the shear bond strength of zirconia, whereas storage condition showed no significant effect on this property (F=1.83, P=0.18). The lowest shear bond strength (14.02 MPa±6.86 MPa) was exhibited by the group treated with RelyX Ultimate resin cement, non-adhesive, and water bath-thermal cycling, whereas the highest shear bond strength (54.12 MPa±8.37 MPa) was displayed by the group treated with RelyX Ultimate resin cement, Scotchbond universal adhesive, and water bath-thermal cycling. CONCLUSIONS: Universal adhesives can improve the durability of the bonding of resin cement to zirconia. If non-self-adhesive resin cement is used without a universal adhe-sive, the durability of the bond will be greatly reduced.
OBJECTIVE: To study the effects of universal adhesives and resin cement on the shear bond strength and durability of zirconia ceramics. METHODS:Zirconia ceramics were sintered into 20 mm×10 mm×10 mm and 10 mm×10 mm×10 mm specimens. The experiment was divided into 12 groups. The two types of specimens were bonded using two variants of resin cement (RelyX Ultimate and Clearfil SAC self-adhesive resin cement), universal adhesives (non-adhesive, Scotchbond uni-versal adhesive, and Clearfil SE One adhesive), and storage conditions (water bath and water bath-thermal cycling). The shear bond strengths were tested, and the fracture morphologies were analyzed. RESULTS: The cement (F=8.41, P<0.01) and adhesive (F=30.34, P<0.01) exerted a significant effect on the shear bond strength of zirconia, whereas storage condition showed no significant effect on this property (F=1.83, P=0.18). The lowest shear bond strength (14.02 MPa±6.86 MPa) was exhibited by the group treated with RelyX Ultimate resin cement, non-adhesive, and water bath-thermal cycling, whereas the highest shear bond strength (54.12 MPa±8.37 MPa) was displayed by the group treated with RelyX Ultimate resin cement, Scotchbond universal adhesive, and water bath-thermal cycling. CONCLUSIONS: Universal adhesives can improve the durability of the bonding of resin cement to zirconia. If non-self-adhesive resin cement is used without a universal adhe-sive, the durability of the bond will be greatly reduced.