Lu Yang1, Bingzhuo Chen1, Hongliang Meng1, Huaiqin Zhang1, Feng He1, Haifeng Xie2, Chen Chen3. 1. Jiangsu Key Laboratory of Oral Diseases, Department of Prosthodontics, Affiliated Hospital of Stomatology, Nanjing Medical University, Nanjing, China. 2. Jiangsu Key Laboratory of Oral Diseases, Department of Prosthodontics, Affiliated Hospital of Stomatology, Nanjing Medical University, Nanjing, China. Electronic address: xhf-1980@126.com. 3. Jiangsu Key Laboratory of Oral Diseases, Department of Endodontics, Affiliated Hospital of Stomatology, Nanjing Medical University, Nanjing, China. Electronic address: ccchicy@njmu.edu.cn.
Abstract
PURPOSE: This study aimed to evaluate bond durability when applying 2 phosphate ester monomer-containing self-adhesive resin cements alone, versus a combination of phosphate ester monomer-containing primer conditioning plus 2 conventional resin cements requiring primers, to zirconia after different artificial aging methods. METHODS: We cemented air-abraded zirconia plates to composite resin cylinders with self-adhesive resin cements (MS; RU) alone or cemented them with traditional resin cements (ZRV; ZVN) after pre-conditioning with a zirconia primer. A shear bond strength (SBS) test were performed after subjecting them to 19 different aging conditions (n = 15) comprising 30,000× thermocycles, air storage at room temperature (RT), water storage at RT, or at 37 °C for 24 h, 1 week, 1, 3, 6, and 12 months. Zirconia powders mixed with zirconia primer or 2 self-adhesive resin cements were characterized by X-ray photoelectron spectroscopy. RESULTS: Groups MS and ZVN obtained the highest SBS after all of aging methods. SBS after 6 months of storage was similar to SBS after 24 h of storage, while both were higher than SBS after 1 year of storage. Water storage at 37 °C provided higher SBS than RT water storage did. We detected a Zr-O-P bond in both self-adhesive resin cement/zirconia powder mixtures. CONCLUSIONS: Application of self-adhesive resin cements alone could be an alternative to pre-conditioning with a zirconia primer followed by the application of conventional resin cements. Formation of Zr-O-P bonds contributed to the bonding improvement of self-adhesive resin cements. Different aging conditions affected SBS values.
PURPOSE: This study aimed to evaluate bond durability when applying 2 phosphate ester monomer-containing self-adhesive resin cements alone, versus a combination of phosphate ester monomer-containing primer conditioning plus 2 conventional resin cements requiring primers, to zirconia after different artificial aging methods. METHODS: We cemented air-abraded zirconia plates to composite resin cylinders with self-adhesive resin cements (MS; RU) alone or cemented them with traditional resin cements (ZRV; ZVN) after pre-conditioning with a zirconia primer. A shear bond strength (SBS) test were performed after subjecting them to 19 different aging conditions (n = 15) comprising 30,000× thermocycles, air storage at room temperature (RT), water storage at RT, or at 37 °C for 24 h, 1 week, 1, 3, 6, and 12 months. Zirconia powders mixed with zirconia primer or 2 self-adhesive resin cements were characterized by X-ray photoelectron spectroscopy. RESULTS: Groups MS and ZVN obtained the highest SBS after all of aging methods. SBS after 6 months of storage was similar to SBS after 24 h of storage, while both were higher than SBS after 1 year of storage. Water storage at 37 °C provided higher SBS than RT water storage did. We detected a Zr-O-P bond in both self-adhesive resin cement/zirconia powder mixtures. CONCLUSIONS: Application of self-adhesive resin cements alone could be an alternative to pre-conditioning with a zirconia primer followed by the application of conventional resin cements. Formation of Zr-O-P bonds contributed to the bonding improvement of self-adhesive resin cements. Different aging conditions affected SBS values.