L H Almeida1, A P N Gomes1, A H Gastmann1, N M Pola1, R R Moraes1, R D Morgental1,2, S S Cava3, A O C Felix3, F G Pappen1. 1. Graduate Program in Dentistry, Federal University of Pelotas, Pelotas, Brazil. 2. Department of Stomatology, School of Dentistry, Federal University of Santa Maria, Santa Maria, Brazil. 3. School of Materials Engineering, Federal University of Pelotas, Pelotas, Brazil.
Abstract
AIM: To evaluate bone tissue reactions in rats to an MTA-based endodontic sealer with and without the addition of various concentrations of C3A or C3A + Ag. METHODOLOGY: Bone tissue reactions were evaluated in 45 Wistar rats after 7, 30 and 90 days (n = 5 per period). Three surgical cavities were prepared on the right femur and filled with 0.2 mL MTA Fillapex, MTA Fillapex + C3A and C3A + Ag at various concentrations: AH Plus (Dentsply DeTrey GmbH, Konstanz, Germany), EndoSequence BC (Brasseler USA, Savannah, GA, USA) or no sealer (negative control). By the end of each experimental period, animals were randomly euthanized. The samples were histologically processed and analysed using a light microscope. The presence of inflammatory cells, fibres and hard tissue barrier formation was evaluated. Data were analysed statistically using nonparametric tests to compare the differences between groups. Multiple groups were compared using the Kruskal-Wallis and Mann-Whitney U-tests with a Bonferroni correction at P = 0.05. RESULTS: The inflammatory response significantly decreased from 30 to 90 days (P < 0.05). Fibre condensation was similar amongst the groups at 07 and 30 days after intervention (P > 0.05). At 90 days, however, fibres were absent in most specimens of EndoSequence BC Sealer, AH Plus, MTA Fillapex and the control group, whilst they were still observed in samples of the modified sealers (P < 0.05). At 90 days, all specimens of AH Plus, EndoSequence BC Sealer and control group had complete formation of hard tissue barrier. In the MTA Fillapex group, as well as in the modified sealers groups, partial deposition of mineralized tissue was noticed. CONCLUSION: The hypothesis tested that the incorporation of C3A and C3A + Ag particles to MTA Fillapex would improve bone tissue repair was partially accepted, since modified MTA Fillapex did not have the same repair potential as the commercial bioceramic material.
AIM: To evaluate bone tissue reactions in rats to an MTA-based endodontic sealer with and without the addition of various concentrations of C3A or C3A + Ag. METHODOLOGY: Bone tissue reactions were evaluated in 45 Wistar rats after 7, 30 and 90 days (n = 5 per period). Three surgical cavities were prepared on the right femur and filled with 0.2 mL MTA Fillapex, MTA Fillapex + C3A and C3A + Ag at various concentrations: AH Plus (Dentsply DeTrey GmbH, Konstanz, Germany), EndoSequence BC (Brasseler USA, Savannah, GA, USA) or no sealer (negative control). By the end of each experimental period, animals were randomly euthanized. The samples were histologically processed and analysed using a light microscope. The presence of inflammatory cells, fibres and hard tissue barrier formation was evaluated. Data were analysed statistically using nonparametric tests to compare the differences between groups. Multiple groups were compared using the Kruskal-Wallis and Mann-Whitney U-tests with a Bonferroni correction at P = 0.05. RESULTS: The inflammatory response significantly decreased from 30 to 90 days (P < 0.05). Fibre condensation was similar amongst the groups at 07 and 30 days after intervention (P > 0.05). At 90 days, however, fibres were absent in most specimens of EndoSequence BC Sealer, AH Plus, MTA Fillapex and the control group, whilst they were still observed in samples of the modified sealers (P < 0.05). At 90 days, all specimens of AH Plus, EndoSequence BC Sealer and control group had complete formation of hard tissue barrier. In the MTA Fillapex group, as well as in the modified sealers groups, partial deposition of mineralized tissue was noticed. CONCLUSION: The hypothesis tested that the incorporation of C3A and C3A + Ag particles to MTA Fillapex would improve bone tissue repair was partially accepted, since modified MTA Fillapex did not have the same repair potential as the commercial bioceramic material.
Authors: Jessica Emanuella Rocha Paz; Priscila Oliveira Costa; Albert Alexandre Costa Souza; Ingrid Macedo de Oliveira; Lucas Fernandes Falcão; Carlos Alberto Monteiro Falcão; Maria Ângela Area Leão Ferraz; Lucielma Salmito Soares Pinto Journal: Restor Dent Endod Date: 2021-09-02