Ahmed Jamleh1, Amjad Alghaihab2, Abdulmohsen Alfadley2, Hussam Alfawaz3, Abdullah Alqedairi3, Khalid Alfouzan2. 1. Restorative and Prosthetic Dental Sciences, College of Dentistry, King Saud bin Abdulaziz University for Health Sciences, National Guard Health Affairs, Riyadh, Kingdom of Saudi Arabia, and King Abdullah International Medical Research Centre, National Guard Health Affairs, Riyadh, Kingdom of Saudi Arabia. Electronic address: aojamleh@gmail.com. 2. Restorative and Prosthetic Dental Sciences, College of Dentistry, King Saud bin Abdulaziz University for Health Sciences, National Guard Health Affairs, Riyadh, Kingdom of Saudi Arabia, and King Abdullah International Medical Research Centre, National Guard Health Affairs, Riyadh, Kingdom of Saudi Arabia. 3. Department of Restorative Dental Sciences, College of Dentistry, King Saud University, Riyadh, Saudi Arabia.
Abstract
INTRODUCTION: The aim of this in vitro study was to compare the cyclic fatigue resistance and torsional resistance of EdgeTaper Platinum (ETP) with those of ProTaper Gold (PTG) at simulated body temperature. METHODS: ETP and PTG files with #25 tip size were selected. Cyclic fatigue tests were performed in a stainless steel artificial canal until file fracture occurred. The time to fracture was recorded. For the torsional resistance testing, the apical 5 mm of the file was firmly secured with acrylic resin, and the assembly was fixed over torque gauge device. A uniform torsional stress was applied with continuous rotation motion until fracture occurred. The torque at failure was recorded. Both experiments were conducted at 35 ± 1°C. Fractured surfaces were tested via scanning electron microscopy. Statistical analysis was performed using independent Student t test at 5% significance level. RESULTS: The ETP had superior cyclic fatigue resistance than PTG (P < .01). However, it exhibited lower torsional resistance (P < .05). The ETP and PTG showed typical features of cyclic and torsional fatigue behavior under scanning electron microscopy. CONCLUSIONS: The ETP exhibited superior resistance to cyclic fatigue but failed to show any improvement in the torsional resistance compared with PTG.
INTRODUCTION: The aim of this in vitro study was to compare the cyclic fatigue resistance and torsional resistance of EdgeTaper Platinum (ETP) with those of ProTaper Gold (PTG) at simulated body temperature. METHODS: ETP and PTG files with #25 tip size were selected. Cyclic fatigue tests were performed in a stainless steel artificial canal until file fracture occurred. The time to fracture was recorded. For the torsional resistance testing, the apical 5 mm of the file was firmly secured with acrylic resin, and the assembly was fixed over torque gauge device. A uniform torsional stress was applied with continuous rotation motion until fracture occurred. The torque at failure was recorded. Both experiments were conducted at 35 ± 1°C. Fractured surfaces were tested via scanning electron microscopy. Statistical analysis was performed using independent Student t test at 5% significance level. RESULTS: The ETP had superior cyclic fatigue resistance than PTG (P < .01). However, it exhibited lower torsional resistance (P < .05). The ETP and PTG showed typical features of cyclic and torsional fatigue behavior under scanning electron microscopy. CONCLUSIONS: The ETP exhibited superior resistance to cyclic fatigue but failed to show any improvement in the torsional resistance compared with PTG.