Nisa Gül Amuk1, Aslı Baysal2, Yakup Üstün3, Gökmen Kurt4. 1. Department of Orthodontics, Erciyes University Faculty of Dentistry, Kayseri, Turkey. 2. Department of Orthodontics, İzmir Katip Çelebi University Faculty of Dentistry, İzmir, Turkey. 3. Department of Restorative Dentistry and Endodontics, Erciyes University Faculty of Dentistry, Kayseri, Turkey. 4. Department of Orthodontics, Bezmialem University Faculty of Dentistry, İstanbul, Turkey.
Abstract
PURPOSE: The aim of this study was to test the null hypothesis that no difference exists between shear bond strength values of control and bleaching plus desensitizer applied groups. MATERIALS AND METHODS: A hundred freshly extracted human premolar teeth were randomly divided into five groups. Group I served as the control group with no bleaching application, while only bleaching was achieved in Group II. Desensitizer containing potassium nitrate-fluoride and casein phosphopeptide amorphous calcium phosphate were applied in Groups III and IV, after bleaching respectively. A bleaching agent containing amorphous calcium phosphate was used in Group V. Shear bond strength tests were carried out using a universal testing machine (Instron Corp., Norwood, MA, USA). Remnant adhesive on the teeth and brackets was examined to score the adhesive remnant index. Kruskal-Wallis and Chi-Square tests were used for statistical analysis of the data. RESULTS: Statistically significant differences were found among the groups for shear bond strength values (p<.001). The shear bond strength of Group III (8.0±2.2 MPa) was significantly lower than the other groups (p<.05). The highest shear bond strength values were found for Group I (13.6±3.7 MPa) and Group IV (12.8±4.0 MPa). No statistically significant difference was observed between Group II (10.0±2.7 MPa) and Group V (10.8±2.9 MPa). The differences between adhesive remnant index scores of the groups were not statistically significant. CONCLUSION: Casein phosphopeptide amorphous calcium phosphate gel application showed a similar shear bond strength value to the control group, while shear bond strength values decreased after using other desensitizers.
PURPOSE: The aim of this study was to test the null hypothesis that no difference exists between shear bond strength values of control and bleaching plus desensitizer applied groups. MATERIALS AND METHODS: A hundred freshly extracted human premolar teeth were randomly divided into five groups. Group I served as the control group with no bleaching application, while only bleaching was achieved in Group II. Desensitizer containing potassium nitrate-fluoride and casein phosphopeptide amorphous calcium phosphate were applied in Groups III and IV, after bleaching respectively. A bleaching agent containing amorphous calcium phosphate was used in Group V. Shear bond strength tests were carried out using a universal testing machine (Instron Corp., Norwood, MA, USA). Remnant adhesive on the teeth and brackets was examined to score the adhesive remnant index. Kruskal-Wallis and Chi-Square tests were used for statistical analysis of the data. RESULTS: Statistically significant differences were found among the groups for shear bond strength values (p<.001). The shear bond strength of Group III (8.0±2.2 MPa) was significantly lower than the other groups (p<.05). The highest shear bond strength values were found for Group I (13.6±3.7 MPa) and Group IV (12.8±4.0 MPa). No statistically significant difference was observed between Group II (10.0±2.7 MPa) and Group V (10.8±2.9 MPa). The differences between adhesive remnant index scores of the groups were not statistically significant. CONCLUSION: Casein phosphopeptide amorphous calcium phosphate gel application showed a similar shear bond strength value to the control group, while shear bond strength values decreased after using other desensitizers.
Authors: Samir E Bishara; Charuphan Oonsombat; Manal M A Soliman; Raed Ajlouni; John F Laffoon Journal: Am J Orthod Dentofacial Orthop Date: 2005-12 Impact factor: 2.650