Degradable Copolymer Nanoparticles from Radical Ring-Opening Copolymerization between Cyclic Ketene Acetals and Vinyl Ethers.

2-Methylene-1,3-dioxepane (MDO) and different vinyl ether (VE) monomers were successfully copolymerized by free-radical radical ring-opening copolymerization (rROP) to yield P(MDO- co-VE) copolymers with Mn = 7 000-13 000 g·mol-1 and high molar fractions of MDO ( FMDO = 0.7-0.9). By using VE derivatives of different aqueous solubilities or by grafting PEG chains onto the copolymers by "click" chemistry via azide-containing VE units, hydrophobic, amphiphilic and water-soluble copolymers were obtained. The different copolymers were then formulated into nanoparticles by nanoprecipitation using Pluronics for hydrophobic copolymers, without surfactant for amphiphilic copolymers, or blended with PMDO for water-soluble copolymers. Most of the copolymers led to nanoparticles with average diameters in the 130-250 nm with narrow particle size distributions and satisfying colloidal stability for a period of at least 1-2 weeks and up to 6 months. The copolymers were successfully degraded under accelerated, hydrolytic or enzymatic conditions. Hydrophobic copolymers led to degradation kinetics in PBS similar to that of PCL and complete degradation (-95% in Mn decrease) was observed in the presence of enzymes (lipases). Preliminary cytotoxicity assays were performed on endothelial cells (HUVEC) and macrophages (J774.A1) and revealed high cell viabilities at 0.1 mg·mL-1.