Gabriella Peñarrieta-Juanito1, Mariane B Sordi1, Bruno Henriques2,3, Marta E R Dotto4, Wim Teughels5, Filipe S Silva3, Ricardo S Magini1, Júlio C M Souza3. 1. Postgraduate Program in Dentistry (PPGO), Department of Dentistry, Division of Implant Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, Brazil. 2. Laboratory of Ceramic and Composite Materials (CERMAT), Department of Mechanical Engineering (EMC), Federal University of Santa Catarina (UFSC), Florianópolis, Brazil. 3. Center for Microelectromechanical Systems (CMEMS-UMINHO), University of Minho, Guimarães, Portugal. 4. Department of Physics, Federal University of Santa Catarina (UFSC), Florianópolis, Brazil. 5. Department of Oral Health Sciences, University Hospitals Leuven, Katholieke Universiteit Leuven, Leuven, Belgium.
Abstract
OBJECTIVE: The aim of this study was to evaluate surface changes on dental implant systems and ions release after immersion in fluoride and hydrogen peroxide. METHODS: Ten implant-abutment assemblies were embedded in acrylic resin and cross-sectioned along the implant vertical axis. Samples were wet ground and polished. Delimited areas of groups of samples were immersed in 1.23% sodium fluoride gel (F) or in 35% hydrogen peroxide (HP) for 16 min. Gels (n = 3) were collected from the implant surfaces and analyzed by inductively coupled plasma mass spectrometry (ICP-MS), to detect the concentration of metallic ions released from the implant systems. Selected areas of the abutment and implant (n = 15) were analyzed by atomic force microscopy (AFM) and scanning electron microscopy (SEM). RESULTS: SEM images revealed surface topographic changes on implant-abutment joints after immersion in fluoride. Implants showed excessive oxidation within loss of material, while abutment surfaces revealed intergranular corrosion after immersion in fluoride. ICP-MS results revealed a high concentration of Ti, Al, V ions in fluoride after contact with the implant systems. Localized corrosion of implant systems could not be detected by SEM after immersion in hydrogen peroxide although the profilometry showed increase in roughness. ICP-MS showed the release of metallic ions in hydrogen peroxide medium after contact with dental implants. CONCLUSION: Therapeutical substances such as fluorides and hydrogen peroxide can promote the degradation of titanium-based dental implant and abutments leading to the release of toxic ions.
OBJECTIVE: The aim of this study was to evaluate surface changes on dental implant systems and ions release after immersion in fluoride and hydrogen peroxide. METHODS: Ten implant-abutment assemblies were embedded in acrylic resin and cross-sectioned along the implant vertical axis. Samples were wet ground and polished. Delimited areas of groups of samples were immersed in 1.23% sodium fluoride gel (F) or in 35% hydrogen peroxide (HP) for 16 min. Gels (n = 3) were collected from the implant surfaces and analyzed by inductively coupled plasma mass spectrometry (ICP-MS), to detect the concentration of metallic ions released from the implant systems. Selected areas of the abutment and implant (n = 15) were analyzed by atomic force microscopy (AFM) and scanning electron microscopy (SEM). RESULTS: SEM images revealed surface topographic changes on implant-abutment joints after immersion in fluoride. Implants showed excessive oxidation within loss of material, while abutment surfaces revealed intergranular corrosion after immersion in fluoride. ICP-MS results revealed a high concentration of Ti, Al, V ions in fluoride after contact with the implant systems. Localized corrosion of implant systems could not be detected by SEM after immersion in hydrogen peroxide although the profilometry showed increase in roughness. ICP-MS showed the release of metallic ions in hydrogen peroxide medium after contact with dental implants. CONCLUSION: Therapeutical substances such as fluorides and hydrogen peroxide can promote the degradation of titanium-based dental implant and abutments leading to the release of toxic ions.
Authors: Alexia Vinel; Antoine Al Halabi; Sébastien Roumi; Hélène Le Neindre; Pierre Millavet; Marion Simon; Constance Cuny; Jean-Sébastien Barthet; Pierre Barthet; Sara Laurencin-Dalicieux Journal: Adv Exp Med Biol Date: 2022 Impact factor: 2.622