Stabilizing Li10SnP2S12/Li Interface via an in Situ Formed Solid Electrolyte Interphase Layer.

Despite the extremely high ionic conductivity, the commercialization of Li10GeP2S12-type materials is hindered by the poor stability against Li metal. Herein, to address that issue, a simple strategy is proposed and demonstrated for the first time, i.e., in situ modification of the interface between Li metal and Li10SnP2S12 (LSPS) by pretreatment with specific ionic liquid and salts. X-ray photoelectron spectroscopy and electrochemical impedance spectroscopy results reveal that a stable solid electrolyte interphase (SEI) layer instead of a mixed conducting layer is formed on Li metal by adding 1.5 M lithium bis(trifluoromethanesulfonyl)imide (LiTFSI)/ N-propyl- N-methyl pyrrolidinium bis(trifluoromethanesulfonyl)imide (Pyr13TFSI) ionic liquid, where ionic liquid not only acts as a wetting agent but also improves the stability at the Li/LSPS interface. This stable SEI layer can prevent LSPS from directly contacting the Li metal and further decomposition, and the Li/LSPS/Li symmetric cell with 1.5 M LiTFSI/Pyr13TFSI attains a stable cycle life of over 1000 h with both the charge and discharge voltages reaching about 50 mV at 0.038 mA cm-2. Furthermore, the effects of different Li salts on the interfacial modification is also compared and investigated. It is shown that lithium bis(fluorosulfonyl) imide (LiFSI) salt causes the enrichment of LiF in the SEI layer and results in a higher resistance of the cell upon a long cycling life.