Maham Muneeb Lone1, Farhan Raza Khan2, Muneeb Ahmed Lone3. 1. Department of Operative Dentistry, Sindh Institute of Oral Health Sciences, Jinnah Sindh Medical University, Karachi. 2. Department of Operative Dentistry, The Aga Khan University Hospital, Stadium Road, Karachi. 3. Department of Prosthodontics, Dow University of Health Sciences (Ojha Campus), Karachi.
Abstract
OBJECTIVE: To compare apical microleakage of extracted, single-rooted teeth obturated with thermoplasticized injectable gutta-percha using two different endodontic sealers (calcium-hydroxide and resin based). STUDY DESIGN: An experimental study. PLACE AND DURATION OF STUDY: The Aga Khan University Hospital (AKUH), Dental Clinics and Laboratory from June to September 2015. METHODOLOGY: The study was conducted using extracted teeth. After access cavities were made, cleaning and shaping of root canals was done in 70 teeth. Teeth were randomly allocated into two groups and obturated with thermoplasticized injectable gutta-percha (Obtura II) using two sealers (Sealapex vs. AH plus). After immersing the teeth in 2.0% methylene blue, they were split longitudinally, viewed under light microscope (magnification X4) and images were taken by a camera connected to microscope. The extent of dye penetration was assessed from apex to its coronal part and recorded in millimeters. Independent sample t-test was used to compare microleakage in the two groups. Pearson correlation coefficient was used for inter-examiner reliability of dye penetration measurements. A p-value of <0.05 was taken as statistically significant. RESULTS: Teeth obturated with Obtura II gutta-percha with AH plus sealer had a mean dye penetration of 1.20 ±0.79 mm. This was significantly better than Obtura II with Sealapex sealer (p=0.003). CONCLUSION: Obtura II-AH plus sealer was a better combination for obturation as it showed a lesser degree of microleakage. Obtura II with Sealapex group showed higher microleakage, so this combination should be avoided in single-rooted teeth.
RCT Entities:
OBJECTIVE: To compare apical microleakage of extracted, single-rooted teeth obturated with thermoplasticized injectable gutta-percha using two different endodontic sealers (calcium-hydroxide and resin based). STUDY DESIGN: An experimental study. PLACE AND DURATION OF STUDY: The Aga Khan University Hospital (AKUH), Dental Clinics and Laboratory from June to September 2015. METHODOLOGY: The study was conducted using extracted teeth. After access cavities were made, cleaning and shaping of root canals was done in 70 teeth. Teeth were randomly allocated into two groups and obturated with thermoplasticized injectable gutta-percha (Obtura II) using two sealers (Sealapex vs. AH plus). After immersing the teeth in 2.0% methylene blue, they were split longitudinally, viewed under light microscope (magnification X4) and images were taken by a camera connected to microscope. The extent of dye penetration was assessed from apex to its coronal part and recorded in millimeters. Independent sample t-test was used to compare microleakage in the two groups. Pearson correlation coefficient was used for inter-examiner reliability of dye penetration measurements. A p-value of <0.05 was taken as statistically significant. RESULTS: Teeth obturated with Obtura II gutta-percha with AH plus sealer had a mean dye penetration of 1.20 ±0.79 mm. This was significantly better than Obtura II with Sealapex sealer (p=0.003). CONCLUSION:Obtura II-AH plus sealer was a better combination for obturation as it showed a lesser degree of microleakage. Obtura II with Sealapex group showed higher microleakage, so this combination should be avoided in single-rooted teeth.