Fahad Alkhudhairy1, Abdulaziz AlKheraif2, Mohammed Bin-Shuwaish1, Sulieman Al-Johany3, Mustafa Naseem4, Fahim Vohra3. 1. 1 Department of Restorative Dental Sciences, College of Dentistry, King Saud University , Riyadh, Saudi Arabia . 2. 2 Dental Health Department, College of Applied Medical Sciences, King Saud University , Riyadh, Saudi Arabia . 3. 3 Department of Prosthetic Dental Science, College of Dentistry, King Saud University , Riyadh, Saudi Arabia . 4. 4 Department of Preventive Dental Sciences, Dar Al Uloom University , Riyadh, Saudi Arabia .
Abstract
BACKGROUND: The available evidence of Er,Cr:YSGG lasers on bleached enamel is limited and controversial. It is assumed that Er,Cr:YSGG laser will be effective in reversing the effect of bleaching on adhesive bond integrity of enamel to resin composite. OBJECTIVE: The study aimed to evaluate the efficacy of Er,Cr:YSGG laser on bond strength and microleakage of bleached enamel. MATERIALS AND METHODS: From the 80 samples, 60 samples were bleached (40% hydrogen peroxide) and divided into three subgroups. Twenty bleached samples in each subgroup were exposed to 10% sodium ascorbate (Gp A), Er,Cr:YSGG laser (50 Hz and 4.5 W) (Gp L), and no treatment (Gp B), respectively. Twenty samples were not bleached (Control-C). Using etch and rinse technique, resin composite was built-up on enamel and photopolymerized. Ten specimens in each group were tested for shear bond strength at a crosshead speed of 1 mm/min. Ten specimens in each group were tested for microleakage using 2% methylene blue. Data were analyzed using analysis of variance (ANOVA) and Tukey post hoc multiple comparisons test. RESULTS: The mean bond strength of specimens in group L (30.83 ± 1.7000) was comparable with group A (31.38 ± 2.03) and was significantly higher than bleached specimens (9.49 ± 0.86) (p < 0.001). The highest mean microleakage values were observed in bleached group (630.32 ± 156.58). The mean microleakage among control (36.66 ± 27.33) and laser group specimens (55.32 ± 34.98) was comparable (p > 0.05). CONCLUSIONS: Treatment of bleached enamel with erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser showed a significant reversal effect on the enamel bond strength and microleakage scores. CLINICAL SIGNIFICANCE: Er,Cr:YSGG laser (50 Hz, 4.5 W) treatment has the potential to restore the bond strength of bleached enamel to resin composite.
BACKGROUND: The available evidence of Er,Cr:YSGG lasers on bleached enamel is limited and controversial. It is assumed that Er,Cr:YSGG laser will be effective in reversing the effect of bleaching on adhesive bond integrity of enamel to resin composite. OBJECTIVE: The study aimed to evaluate the efficacy of Er,Cr:YSGG laser on bond strength and microleakage of bleached enamel. MATERIALS AND METHODS: From the 80 samples, 60 samples were bleached (40% hydrogen peroxide) and divided into three subgroups. Twenty bleached samples in each subgroup were exposed to 10% sodium ascorbate (Gp A), Er,Cr:YSGG laser (50 Hz and 4.5 W) (Gp L), and no treatment (Gp B), respectively. Twenty samples were not bleached (Control-C). Using etch and rinse technique, resin composite was built-up on enamel and photopolymerized. Ten specimens in each group were tested for shear bond strength at a crosshead speed of 1 mm/min. Ten specimens in each group were tested for microleakage using 2% methylene blue. Data were analyzed using analysis of variance (ANOVA) and Tukey post hoc multiple comparisons test. RESULTS: The mean bond strength of specimens in group L (30.83 ± 1.7000) was comparable with group A (31.38 ± 2.03) and was significantly higher than bleached specimens (9.49 ± 0.86) (p < 0.001). The highest mean microleakage values were observed in bleached group (630.32 ± 156.58). The mean microleakage among control (36.66 ± 27.33) and laser group specimens (55.32 ± 34.98) was comparable (p > 0.05). CONCLUSIONS: Treatment of bleached enamel with erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser showed a significant reversal effect on the enamel bond strength and microleakage scores. CLINICAL SIGNIFICANCE: Er,Cr:YSGG laser (50 Hz, 4.5 W) treatment has the potential to restore the bond strength of bleached enamel to resin composite.
Entities:
Keywords:
Er,Cr:YSGG laser; bleached enamel; bond strength; microleakage; resin composite