Preparation and characterisation of activated carbon from waste tea by physical activation using steam.

In this study, the feasibility of preparing activated carbon from waste tea by physical activation using steam was investigated. The effects of activation temperature on yield and pore properties of the prepared activated carbon were studied. The yield decreased with increased activation temperature owing to the decomposition of cellulose and hemicellulose. The specific surface area and pore volume of the activated carbon were estimated using the Brunauer-Emmett-Teller method, Langmuir equation, and t-plot method. The specific surface area and micropore volume increased with increases in activation temperature, as additional volatile materials were released. The specific surface area significantly decreased at first but slightly increased with increasing activation time. The maximum specific surface area reached 995 m2/g at an activation temperature of 800 °C with a water flow rate of 0.075 g/min and a constant hold time of 0.5 hr. According to the nitrogen adsorption isotherms, micropores mainly developed when the activation temperature was below 800 °C, and both micropores and mesopores developed when it was above 800 °C. The results showed that activation temperature significantly affected micropore and mesopore volumes, as well as the specific surface area of the activated carbon. Overall, waste tea was found to be an attractive raw material for producing low-cost activated carbon. Implications: Every year, a large amount of waste tea is generated after extraction. The high carbon content of waste tea showed that it can be used as raw material to produce activated carbon. This study investigated the feasibility of preparing activated carbon from waste tea by physical activation using steam. Temperature and time were found to have clear effects on pore properties. Our proposed method and raw material are more environmentally friendly and involve low cost. Furthermore, this offers a potential solution to the problems of waste tea disposal and low-cost activated carbon production.