AIM: To investigate the effect of different toothpaste formulations used prior to dental bleaching with 35% hydrogen peroxide (HP) on the mineral content and surface morphology of enamel. METHODS: Seventy bovine enamel blocks (4×4×2 mm) were submitted to in vitro treatment protocols using a toothbrushing machine prior to dental bleaching or a placebo procedure (n=10) as proposed in the following groups: unbleached control (PLA), bleached control (HP), and brushing with differing toothpastes prior to HP bleaching, including: potassium nitrate toothpaste containing sodium fluoride (PN), sodium monofluorophosphate/MFP toothpaste (FT), arginine-carbonate (8% arginine) (PA) or arginine-carbonate (1.5% arginine) toothpaste (SAN), and toothpaste containing bioactive glass (NM). Phosphorus concentration in gel ([P]) was evaluated (μg of P/mg of gel), and the elemental levels (wt%) of Ca, P, and Na as well as the proportion between Ca and P and spectra graphics were determined using an energy-dispersive X-ray spectrometer (EDS). The surface morphology was assessed using scanning electron microscopy (SEM). The data were subjected to analysis of variance and the Tukey test (α=0.05). RESULTS: HP demonstrated the greatest [P] values in gel, being statistically different from PLA. The [P] of NM was statistically similar to PLA. HP showed a significant decrease in the Ca% and Ca/P values when compared to PLA in EDS analysis. PA showed Ca/P values statistically different from HP. In accordance with SEM analysis, the PA, SAN, and NM groups presented a smooth and uniform enamel surface, while HP and FT demonstrated some alterations in morphology. CONCLUSION: The toothpastes containing bioactive glass or arginine carbonate used prior to dental bleaching were effective in protecting enamel against mineral loss promoted by the whitening procedure.
AIM: To investigate the effect of different toothpaste formulations used prior to dental bleaching with 35% hydrogen peroxide (HP) on the mineral content and surface morphology of enamel. METHODS: Seventy bovine enamel blocks (4×4×2 mm) were submitted to in vitro treatment protocols using a toothbrushing machine prior to dental bleaching or a placebo procedure (n=10) as proposed in the following groups: unbleached control (PLA), bleached control (HP), and brushing with differing toothpastes prior to HP bleaching, including: potassium nitrate toothpaste containing sodium fluoride (PN), sodium monofluorophosphate/MFP toothpaste (FT), arginine-carbonate (8% arginine) (PA) or arginine-carbonate (1.5% arginine) toothpaste (SAN), and toothpaste containing bioactive glass (NM). Phosphorus concentration in gel ([P]) was evaluated (μg of P/mg of gel), and the elemental levels (wt%) of Ca, P, and Na as well as the proportion between Ca and P and spectra graphics were determined using an energy-dispersive X-ray spectrometer (EDS). The surface morphology was assessed using scanning electron microscopy (SEM). The data were subjected to analysis of variance and the Tukey test (α=0.05). RESULTS: HP demonstrated the greatest [P] values in gel, being statistically different from PLA. The [P] of NM was statistically similar to PLA. HP showed a significant decrease in the Ca% and Ca/P values when compared to PLA in EDS analysis. PA showed Ca/P values statistically different from HP. In accordance with SEM analysis, the PA, SAN, and NM groups presented a smooth and uniform enamel surface, while HP and FT demonstrated some alterations in morphology. CONCLUSION: The toothpastes containing bioactive glass or arginine carbonate used prior to dental bleaching were effective in protecting enamel against mineral loss promoted by the whitening procedure.