PURPOSE: To compare marginal and internal adaptations of porcelain laminate veneers fabricated with heat-pressed and CAD/CAM techniques, and to evaluate the clinical performances 2 years after cementation. MATERIALS AND METHODS: Thirty heat-pressed and 31 CAD/CAM porcelain laminate veneers were fabricated for 12 patients. Silicone replicas of each veneer were obtained. Replicas were sectioned into 4 parts to measure adaptations of the veneers. A stereomicroscope was used to measure from 3 locations of replicas for marginal, and 9 locations for internal adaptations at 40x magnification. Clinical evaluations were done at baseline and 6, 12, 18, and 24 months after cementation according to the modified United States Public Health Service (USPHS) criteria. Independent samples t-test compared the adaptation values between heat-pressed and CAD/CAM groups. Paired t-test was used to evaluate marginal and internal adaptations of each group. Differences between the modified USPHS criteria ratings of heat-pressed and CAD/CAM groups were determined by the Mann-Whitney U test. Kaplan-Meier analysis was used to analyze the survival ratings of the veneers (p < 0.05). RESULTS: The mean marginal adaptation values of heat-pressed and CAD/CAM veneers were 295 and 314.98 μm, respectively, and there was no statistically significant difference (p = 0.541). Internal adaptation values of groups were not statistically different either (201.82 μm for heat pressed; 195.47 μm for CAD/CAM p = 0.734). When marginal and internal adaptation values were compared within groups, there were significant differences both for heat-pressed (p < 0.001) and CAD/CAM (p < 0.001). All veneers were rated 100% satisfactory during the 2-year period. CONCLUSION: Within the limitations of this study, fabrication method, whether CAD/CAM or heat-pressed, had no effect on the marginal and internal adaptation of porcelain laminate veneers. The results showed that both fabrication techniques performed well after 2 years of clinical performance.
PURPOSE: To compare marginal and internal adaptations of porcelain laminate veneers fabricated with heat-pressed and CAD/CAM techniques, and to evaluate the clinical performances 2 years after cementation. MATERIALS AND METHODS: Thirty heat-pressed and 31 CAD/CAM porcelain laminate veneers were fabricated for 12 patients. Silicone replicas of each veneer were obtained. Replicas were sectioned into 4 parts to measure adaptations of the veneers. A stereomicroscope was used to measure from 3 locations of replicas for marginal, and 9 locations for internal adaptations at 40x magnification. Clinical evaluations were done at baseline and 6, 12, 18, and 24 months after cementation according to the modified United States Public Health Service (USPHS) criteria. Independent samples t-test compared the adaptation values between heat-pressed and CAD/CAM groups. Paired t-test was used to evaluate marginal and internal adaptations of each group. Differences between the modified USPHS criteria ratings of heat-pressed and CAD/CAM groups were determined by the Mann-Whitney U test. Kaplan-Meier analysis was used to analyze the survival ratings of the veneers (p < 0.05). RESULTS: The mean marginal adaptation values of heat-pressed and CAD/CAM veneers were 295 and 314.98 μm, respectively, and there was no statistically significant difference (p = 0.541). Internal adaptation values of groups were not statistically different either (201.82 μm for heat pressed; 195.47 μm for CAD/CAM p = 0.734). When marginal and internal adaptation values were compared within groups, there were significant differences both for heat-pressed (p < 0.001) and CAD/CAM (p < 0.001). All veneers were rated 100% satisfactory during the 2-year period. CONCLUSION: Within the limitations of this study, fabrication method, whether CAD/CAM or heat-pressed, had no effect on the marginal and internal adaptation of porcelain laminate veneers. The results showed that both fabrication techniques performed well after 2 years of clinical performance.
Authors: Ali Al-Rimawi; Mostafa EzEldeen; Danilo Schneider; Constantinus Politis; Reinhilde Jacobs Journal: Int J Environ Res Public Health Date: 2019-02-11 Impact factor: 3.390