Inverted Planar Perovskite Solar Cells with a High Fill Factor and Negligible Hysteresis by the Dual Effect of NaCl-Doped PEDOT:PSS.

The performance of inverted perovskite solar cells is highly dependent on hole extraction and surface properties of hole transport layers. To highlight the important role of hole transport layers, a facile and simple method is developed by adding sodium chloride (NaCl) into poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS). The average power conversion efficiency of the perovskite solar cells prepared on NaCl-doped PEDOT:PSS is 17.1% with negligible hysteresis, compared favorably to the control devices (15.1%). Particularly, they exhibit markedly improved Voc and fill factor (FF), with the best FF as high as 81.9%. The enhancement of photovoltaic performance is ascribed to two effects. Better conductivity and hole extraction of PEDOT:PSS are observed after NaCl doping. More intriguingly, the perovskite polycrystalline film shows a preferred orientation along the (001) direction on NaCl-doped PEDOT:PSS, leading to a more uniform thin film. The comparison of the crystal structure between NaCl and MAPbCl3 indicates a lattice constant mismatch less than 2% and a matched chlorine atom arrangement on the (001) surface, which implies that the NaCl crystallites on the top surface of PEDOT:PSS might serve as seeds guiding the growth of perovskite crystals. This simple method is fully compatible with printing technologies to mass-produce perovskite solar cells with high efficiency and tunable crystal orientations.