Fatih Tulumbacı1, Volkan Arıkan2, Aylin Akbay Oba2, Serdar Bağlar3. 1. Ankara Yıldırm Beyazıt University of Dentistry, Department of Pediatric Dentistry, Ankara, Turkey. 2. Kırıkkale University Faculty of Dentistry, Department of Pediatric Dentistry, Kırıkkale, Turkey. 3. Kırıkkale University Faculty of Dentistry, Restorative Dentistry, Kırıkkale, Turkey.
Abstract
Introduction: The aim of the present study was to evaluate and compare the effect of acidetchingand Er, Cr:YSGG laser treatment before the reattachment of incisal fragments in coronal fractures of permanent incisor teeth. Methods:Sixty-six sound human maxillary incisors were randomly divided into 3 groups (n=22). Teeth were embedded in self-cure acrylic resins by leaving one-third of the crowns out, and uncomplicated crown fractures were obtained using an Instron testing device. The fragments were reattached using 3 different procedures and a hybrid resin composite (Z250): Group I: Acid etching + Prime & Bond NT; Group II: Er,Cr:YSGG + Prime & Bond NT; Group III: Er,Cr:YSGG + Acid etching + Prime & Bond NT. The percentages of shear bond strengths were determined by comparing fracture strengths of sound and reattached teeth for 3 groups. All data were analyzed statistically with Kruskal-Wallis H test. Results:Mean fracture strengths of the reattached fragments were between 51.02% and 62.93% of that of the sound teeth in all groups. Group I had significantly higher percentages of shear bond strength values (P<0.05) when compared to group II and group III. No significant difference (P>0.05) was found between group II and group III. Conclusion: The findings of the present study show that Er,Cr:YSGG laser irradiation prior to the reattachment of incisal fragments has a negative effect on fracture strength.
RCT Entities:
Introduction: The aim of the present study was to evaluate and compare the effect of acidetching and Er, Cr:YSGG laser treatment before the reattachment of incisal fragments in coronal fractures of permanent incisor teeth. Methods: Sixty-six sound human maxillary incisors were randomly divided into 3 groups (n=22). Teeth were embedded in self-cure acrylic resins by leaving one-third of the crowns out, and uncomplicated crown fractures were obtained using an Instron testing device. The fragments were reattached using 3 different procedures and a hybrid resin composite (Z250): Group I: Acid etching + Prime & Bond NT; Group II: Er,Cr:YSGG + Prime & Bond NT; Group III: Er,Cr:YSGG + Acid etching + Prime & Bond NT. The percentages of shear bond strengths were determined by comparing fracture strengths of sound and reattached teeth for 3 groups. All data were analyzed statistically with Kruskal-Wallis H test. Results: Mean fracture strengths of the reattached fragments were between 51.02% and 62.93% of that of the sound teeth in all groups. Group I had significantly higher percentages of shear bond strength values (P<0.05) when compared to group II and group III. No significant difference (P>0.05) was found between group II and group III. Conclusion: The findings of the present study show that Er,Cr:YSGG laser irradiation prior to the reattachment of incisal fragments has a negative effect on fracture strength.