Spectroscopy and enhanced frequency upconversion in Nd3+-Yb3+ codoped TPO glasses: energy transfer and NIR to visible upconverter.

TeO2-Pb3O4 (TPO) glasses codoped with Nd3+ and Yb3+ ions have been fabricated by conventional melting technique. The absorption, emission and excitation spectra of the samples have been recorded. The optical band gap in both the doped/codoped glasses is found to be ∼3.31 eV. Judd-Ofelt analysis has been carried out by using the absorption spectrum of 0.8 mol% Nd3+ doped glass to determine the radiative properties viz radiative transition probabilities, branching ratios, radiative lifetimes, quality factor and emission cross sections of some emitting levels for Nd3+ ions. The radiative transition probability for the 4G7/2 → 4I9/2 transition (∼1926 Hz) is found to be maximum compared to other 4G5/2 → 4I9/2 (∼1622 Hz) and 4F5/2 → 4I9/2 (∼865 Hz) transitions. Upconversion (UC) luminescence of the samples has been examined by the 980 nm CW diode laser excitation. Effect of addition of Yb3+ ions in the Nd3+ doped glasses on UC emission intensity has been discussed. The UC emission intensity corresponding to the green, red and NIR bands in the codoped glass has been enhanced by ∼17, ∼12 and ∼42 times as compared to that of the Nd3+ singly doped glass. The quantum efficiency for the 4G7/2 level is found to be ∼32%. The nephelauxetic ratio, bonding parameter and covalency of Nd3+ ions have been found positive which represents the covalent bonding between Nd3+ ion and oxygen atom. The colour tunability from yellowish-green to dominant green region has been obtained in the optimized codoped TPO glass.