Open-Framework Manganese(II) and Cobalt(II) Borophosphates with Helical Chains: Structures, Magnetic, and Luminescent Properties.

Two borophosphates, (NH4)1-2xM1+x(H2O)2(BP2O8)·yH2O with M = Mn (I) and Co (II), synthesized hydrothermally crystallize in enantiomorphous space groups P6522 and P6122 with a = 9.6559(3) and 9.501(3) Å, c = 15.7939(6) and 15.582(4) Å, and V = 1275.3(1) and 1218.2(8) Å3 for I and II, respectively. Both compounds feature helical chains composed of vertex-sharing tetrahedral PO4 and BO4 groups that are connected through O atoms to transition-metal cations, Mn2+ and Co2+, respectively. For the two crystallographically distinct transition-metal cation sites present in the structure, this results in octahedral coordination with different degrees of distortion from the ideal symmetry. The crystal-field parameters, calculated from the corresponding absorption spectra, indicate that Mn2+ and Co2+ ions are located in a weak octahedral-like crystal field and suggest that the Co-ligand interactions are more covalent than the Mn-ligand ones. Luminescence measurements at room temperature reveal an orange emission that red-shifts upon lowering of the temperature to 77 K for I, while II is not luminescent. The luminescence lifetimes of I are 33.4 μs at room temperature and 1.87 ms at 77 K. Both compounds are Curie-Weiss paramagnets with negative Weiss constants and effective magnetic moments expected for noninteracting Mn2+ and Co2+ cations but no clear long-range magnetic order above 2 K.