Effect of Arsenic on the Formation and Adsorption Property of Ferric Hydroxide Precipitates in ZVI Treatment.

Treatment of arsenic by zerovalent iron (ZVI) has been studied extensively. However, the effect of arsenic on the formation of ferric hydroxide precipitates in the ZVI treatment has not been investigated. We discovered that the specific surface area (ca. 187 m2/g) and arsenic content (ca. 67 mg/g) of the suspended solids (As-containing solids) generated in the ZVI treatment of arsenic solutions were much higher than the specific surface area (ca. 37 m2/g) and adsorption capacity (ca.12 mg/g) of the suspended solids (As-free solids) generated in the arsenic-free solutions. Arsenic in the As-containing solids was much more stable than the adsorbed arsenic in As-free solids. XRD, SEM, TEM, and selected area electron diffraction (SAED) analyses showed that the As-containing solids consisted of amorphous nanoparticles, while the As-free solids were composed of micron particles with weak crystallinity. Extended X-ray absorption fine structure (EXAFS) analysis determined that As(V) was adsorbed on the As-containing suspended solids and magnetic solid surfaces through bidentate binuclear complexation; and As(V) formed a mononuclear complex on the As-free suspended solids. The formation of the surface As(V) complexes retarded the bonding of free FeO6 octahedra to the oxygen sites on FeO6 octahedral clusters and prevented the growth of the clusters and their development into 3-dimensional crystalline phases.