Evaluation of pH and calcium ion diffusion from calcium hydroxide pastes and MTA.

The aim of this ex vivo study was to evaluate changes in pH and calcium ion diffusion through root dentin from calcium hydroxide (Ca (OH) 2) and mineral trioxide aggregate (MTA) pastes at 7, 30 and 60 days; and the relationship between pH and ion diffusion. Thirty-two human premolars were used. Crowns were sectioned and root canals instrumented and filled in with the following preparations: 1) Ca(OH) 2 + distilled water (n=7); 2) Ca(OH) 2 + 0.1% chlorhexidine gluconate (n=7); 3) MTA + distilled water (n=7); 4) MTA + 0.1% chlorhexidine gluconate (CHX) (n=7); 5) distilled water (n=2) (control); 6) 0.1% chlorhexidine gluconate (n=2) (control). The apex and coronary opening were sealed with IRM. Roots were placed in Eppendorf tubes with 1 ml distilled water at 37°C and 100% humidity. At baseline, 7, 30 and 60 days, pH was measured with pH meter, and calcium ion content in the solution was analyzed by atomic absorption spectrophotometry. The data were statistically analyzed using ANOVA, simple linear regression analysis and Pearson's correlation test. The highest pH values were achieved with calcium hydroxide pastes at 60 days (p ≤ 0.05). Calcium ions were released in all groups. The calcium hydroxide paste with distilled water at 60 days had the highest calcium ion value (p ≤ 0.01). There was a positive correlation between calcium and pH values. Sociedad Argentina de Investigación Odontológica.