Influence of W substitution on crystal structure, phase evolution and microwave dielectric properties of (Na0.5Bi0.5)MoO4 ceramics with low sintering temperature.

In this work, the (Na0.5Bi0.5)(Mo1-xWx)O4 (x = 0.0, 0.5 and 1.0) ceramics were prepared via solid state reaction method. All the samples can be well densified at sintering temperature about ~720 °C. Dense and homogeneous microstructure with grain size lying between 2~8 μm can be observed from scanning electron microscopy (SEM). Microwave dielectric permittivity of the (Na0.5Bi0.5)(Mo0.5W0.5)O4 ceramic was found to be temperature-independent in a wide range between 25~120 °C with a temperature coefficient of frequency (TCF) ~-6 ppm/°C, a permittivity ~28.9, and Qf values 12,000~14,000 GHz. Crystal structure was refined using Rietveld method and lattice parameters are a = b = 5.281 (5) Å and c = 11.550 (6) Å with a space group I 41/a (88). The (Na0.5Bi0.5)(Mo1-xWx)O4 ceramics might be good candidate for low temperature co-fired ceramics (LTCC) technology.

Introduction

Microwave dielectric ceramics usually possess large dielectric permittivity (εr, compared with that of polymer), small temperature coefficient of frequency (TCF) and low dielectric loss (high quality factor Qf). In recent forty years, microwave dielectric ceramics have been extensively employed as dielectric resonator (DR), dielectric filter, duplexer, dielectric waveguide, dielectric substrate and etc. in mobile communication, radar and global position system (GPS) and other satellite navigation guiding and positioning systems. High integration and miniaturization of modern microwave devices also benefit from the fast development of microwave dielectric materials[1-3].

In the past forty years, large amount of microwave dielectrics have been explored, such as (Mg,Ca)TiO3 system with εr~20, Ba(Mg,Zn)(Ta,Nb)O3 system with εr~30–40, (Zr,Sn)TiO4 system with εr~40–45, (Sr,Ca)TiO3-(La,Nd)AlO3 system with εr~45, and BaO-(Sm,Nd)2O3-TiO2 system with εr above 70[4-8]. However, the high sintering temperature of traditional microwave dielectric ceramics are not suitable for the fast developing modern fabrication technology, low temperature co-fired ceramics (LTCC) technology[2, 3]. Although many lead-rich microwave dielectric ceramics possess low sintering temperature, their toxicity has limited their wide application[9-13]. In recent ten years, the so-called ultra-low temperature co-fired ceramics (ULTCC) technology has attracted much attention due to their intrinsic low firing temperature below base metals’ melting points, such as Al (~660 °C) and Ag (~961 °C)[14, 15]. The top two biggest ULTCC families are Te-rich and Mo-rich series[14-17]. Considering the environmental friendless and price advantage, Mo-rich ULTCC will play an important role in the high integrated electronic devices. Among them, a big family with scheelite-related structure has attracted much attention. Scheelite structure derive from natural mineral CaWO4 and got its name after the discoverer chemist C.W. Scheele from Sweden. The typical formula of scheelite structure is ABO4, in which A site can be alkali metal ions, alkaline earth metal ions, some trivalent metal ions, such as Li, Na, Ba, Sr, Ca, Bi etc., with eight coordination number and B site can be trivalent, pentavalent or six valence metal ion, such as Fe, Ga V, Mo, W etc., with four coordination number[18]. Meanwhile, the anion O can also be replaced partially by F or N. Scheelite structure is quite adaptive like perovskite structure in ABO3 systems. High concentration as large as 1/3 of defects can be introduced into scheelite structure’s A site, in which the formula can be written as A1−xΦxMoO4. Defects and substitutions can cause the ordering at A site, such as (K0.5Eu0.5)MoO4 and Bi2/3Φ1/3MoO4 [19-24]. As reported in literatures, large difference of ionic radius at B site also results in the ordering of [BO4] arrangement at B site, such as Bi(Fe1/3Mo2/3)O4 [25]. High adaptability of scheelite structure can provide large amount of data to study its structure-property relation. In 2006 and 2007[26, 27], Hong et al. first reported microwave dielectric properties and sintering behaviors of the scheelite structured (Ca,Sr,Ba)(W,Mo)O4 ceramics with sintering temperature below 1100 °C, dielectric permittivity between 8~11, Qf values between 30,000 GHz~90,000 GHz, TCF values between −40~−80 ppm/°C. Large negative TCF values limit their application. Subsequently, a series of A site complex substitutions compositions with scheelite structure were reported to possess positive TCF values in our previous work, such as the (Li0.5Bi0.5)MoO4 (εr = 44.4, Qf = 3,200 GHz and TCF = +245 ppm/°C), (Na0.5Bi0.5)MoO4 (εr = 34.4, Qf = 12,300 GHz and TCF = +43 ppm/°C) and (Ag0.5Bi0.5)MoO4 (εr = 30, Qf = 12,600 GHz and TCF = +57 ppm/°C)[28, 29]. When the B site is occupied by W, the (Li0.5Bi0.5)WO4 and (Ag0.5Bi0.5)WO4 compositions crystallize in wolframite structure[30] and only the (Na0.5Bi0.5)WO4 still keep scheelite structure[31]. These results offer the opportunity to design temperature stable scheelite structured microwave dielectric ceramics and study the relation between structure and TCF values. Besides the wide range adjustability of permittivity, Qf and TCF values, low sintering temperature below 700 °C is also a highlight for the Mo-based scheelite materials. In the present work, phase evolution, crystal structure, microstructure, microwave dielectric properties and their relation in the (Na0.5Bi0.5)(Mo1−xWx)O4 (x = 0.0, 0.5 and 1.0) system were studied in detail.

XRD patterns of the (Na0.5Bi0.5)(Mo1−xWx)O4 (x = 0.0, 0.5 and 1.0) ceramics sintered at 720 °C for 2 h are presented in Fig. 1(a). All the samples crystallized in standard tetragonal scheelite structure, in which Na+ and Bi3+ randomly occupied 8-coordinated A site and Mo6+ and W6+ randomly occupied 4-coordinated B site. This result is similar to the literatures’ reports[32-34]. This result indicates that tetragonal scheelite structured solid solution was formed in full composition range in the (Na0.5Bi0.5)(Mo1−xWx)O4 ceramics. To study the crystal structure details of x = 0.5 composition, refinements were performed by using Fullprof software[35] based on refined XRD data. Measured and calculated XRD patterns are presented in Fig. 1(b). As listed in Table 1, refined cell parameters are a = b = 5.281 (5) Å and c = 11.550 (6) Å. with a space group I41/a (No. 88) and acceptable Rp = 9.08%, Rwp = 9.95% and Rexp = 6.25% using the data (ICSD #67491) reported by Teller as starting model[36]. Cell parameters of the (Na0.5Bi0.5)MoO4 and (Na0.5Bi0.5) WO4 are a = b = 5.274 (4) Å, c = 11.578 (2) Å and a = b = 5.282 Å, c = 11.50 Å, respectively, as reported by Hanuza, Waskowska et al.[31, 37, 38]. In scheelite structure, Mo6+ is 4-coordinated and its ionic radius is 0.41 Å, while the ionic radius of W6+ is 0.60 Å[39]. Hence it is understandable that cell parameters changed almost linearly with W6+ substitution concentration.

Figure 1

XRD patterns of the (Na0.5Bi0.5)(Mo1−xWx)O4 (x = 0.0, x = 0.5 and x = 1.0) ceramics (a), the experimental (circles) and simulated (line) XRD patterns of the (Na0.5Bi0.5)(Mo0.5W0.5)O4 composition sintered at 720 °C using space group I 41/a (88) (Rp = 9.08%, Rwp = 9.95%, Rexp = 6.25%) (b) (The short vertical lines represent Bragg reflection positions. The continuous line at the bottom shows the difference between experimental and simulated intensity).

Table 1

Refined atomic fractional coordinates from XRD data of the (Na0.5Bi0.5)(Mo0.5W0.5)O4 ceramic and the cell parameters are a = b = 5.281 (5) Å, c = 11.550 (6) Å with a space group is I 41/a (88).

Atom	Site	Occ.	x	y	z	Biso
Na	4b	0.125	0.00000	0.25000	0.62500	0.75528
Bi	4b	0.125	0.00000	0.25000	0.62500	0.75528
Mo	4a	0.125	0.00000	0.25000	0.12500	0.60363
W	4a	0.125	0.00000	0.25000	0.12500	0.60363
O	16 f	1.000	0.1491(9)	0.0041(1)	0.2089(5)	0.75169

Microstructures of the (Na0.5Bi0.5)(Mo1−xWx)O4 (x = 0.0, 0.5 and 1.0) ceramics sintered at 720 °C for 2 h are shown in Fig. 2. Dense and homogeneous microstructure can be observed, which means that all the ceramics could be well densified at a low sintering temperature ~720 °C. There is no apparent change trend of grains versus substitution of W and it lied between 2~8 µm.

Figure 2

SEM images of the (Na0.5Bi0.5)(Mo1−xWx)O4 (a) x = 0.0 (fractured surface), (b) x = 0.5 and (c) x = 1.0 ceramics sintered at 720 °C for 2 hr.

Phase compositions, sintering temperatures and microwave frequency dielectric properties of the (A0.5Bi0.5)(Mo,W)O4 (A = Li, Na and Ag) ceramics were listed in Table 2  [28–30, 40, 41]. The microwave dielectric properties of (Na0.5Bi0.5)WO4 were first reported here with a ɛr~25.7, a Qf value ~17,500 GHz and a τf value ~− 18 ppm/°C. Although the permittivity of (Na0.5Bi0.5)WO4 ceramic is a little smaller than that of (Na0.5Bi0.5)MoO4 ceramic, its Qf value is 1.4 times larger than that of the (Na0.5Bi0.5)MoO4 ceramic. It must be noted that their TCF values are opposite and this provides an opportunity to design a temperature stable (Na0.5Bi0.5)(Mo0.5W0.5)O4 solid solution ceramic with a ɛr~28.9, a Qf value ~14,000 GHz and a τf value ~−6 ppm/°C as listed in Table 2. As mentioned above, full solid solution can be formed in the (Na0.5Bi0.5)(Mo1−xWx)O4 ceramics. It is quite different from the situation in (Li0.5Bi0.5)(Mo1−xWx)O4 system, in which composite samples were formed. Besides, it is also quite different from the situation in (Ag0.5Bi0.5)(Mo1−xWx)O4 system, in which limited solid solution were formed. Compared with composite method, solid solution method is more controllable. Change of permittivity might be explained by Shannon’s additive rule[42]. According to Shannon’s results, the polarizabilities α of (Na0.5Bi0.5)(Mo1−xWx)O4 could be calculated as follows:where , , , and are the polarizabilities of Bi3+, O2−, Mo6+, Na+ and W6+, respectively[26, 27, 42]. Using the Clausius-Mossotti relation, the relation between dielectric permittivity εr, polarizability αx, cell volume Vx, and the dielectric constant are obtained as following:in which Vx is cell volume and εx is the permittivity of (Na0.5Bi0.5)(Mo1−xWx)O4 ceramics. The calculated molecular polarzabilites from equations (1) and (2) and macroscopical microwave dielectric properties were listed in Table 3. Because the ionic polarizability of Mo6+ is larger than that of W6+, it is understandable that permittivity decreased with increase of W content. The relative error of molecular polarzability is below 13%, which is acceptable and might be attributed to the specific ion neighboring environment. To better understand the scheelite solid solubility here, the phase compositions, sintering temperatures and microwave dielectric properties of the (A0.5Bi0.5)(Mo,W)O4 (A = Li, Na, K and Ag) ceramics are presented in Table 2 in order of ionic radius of A+. It is seen that the scheelite solid solubility is influenced both by the equivalent ionic radius on A and B sites. According to our previous work, scheelite solid solubility is less than 40% in the (Li0.5Bi0.5)(Mo1−xWx)O4 system and possibly larger than 50% in the (Ag0.5Bi0.5)(Mo1−xWx)O4 system, while scheelite solid solution was formed in the whole composition range in (Na0.5Bi0.5)(Mo1−xWx)O4 system here. According to Errandonea and Manjon’ review ref. 43, structures of ABX4 materials are determined both by the ionic radius of A, B, and X ions and the pressure. It is not easy to give a simple structural factor for scheelite structure, such as the famous tolerance factor defined as (RA + RO)/(RB + RO) in perovskite structure[44]. Anyway, from the experimental data listed in Table 2, we can only give a conclusion that scheelite structure can only be kept within a limited range of radius of ions on both A and B sites in oxides. The microwave dielectric permittivities and Qf values of (Na0.5Bi0.5)(Mo1−xWx)O4 (x = 0, 0.5, 1.0) ceramics as a function of temperature are shown in Fig. 3. It is clearly seen that substitution of W for M in the (Na0.5Bi0.5)MoO4 ceramic efficiently modify the temperature dependence of permittivity. In a wide temperature range 20~120 °C, the permittivity of (Na0.5Bi0.5)(Mo0.5W0.5)O4 ceramic changed slightly around 28.9, while Qf values above 12,000 GHz. It is interesting to note that no matter in forms of solid solution or composite, TCF values can be easily tailored to be near zero in the (A0.5Bi0.5)(Mo,W)O4 (A = Li, Na, K and Ag) systems, which makes them possible in fabrication of temperature stable devices. Infrared reflectivity fitting was also employed to study the intrinsic dielectric properties and details were presented in Supplemental Information. Bi3+ neighboring structure was found to account for the shift of macroscopical permittivity due to the large polarization ~6.12 Å3, which is larger than that of Mo6+ and W6+ ions (3.28 and 3.2 Å3, respectively)[26, 27, 42].

Table 2

Phase compositions, sintering temperatures (S. T.) and Microwave dielectric properties of the (A0.5Bi0.5)(Mo,W)O4 (A = Li, Na, K and Ag) ceramics.

Composition	Phase	S.T. (°C)	εr	Qf (GHz)	TCF (ppm/°C)	A site radius	B site Radius	Refs
(Li0.5Bi0.5)MoO4	scheelite	560	44.4	3,200	+245	1.045	0.41	28
(Li0.5Bi0.5)(Mo0.4W0.6)O4	composite	620	31.5	8,500	+20	1.045	0.416	30
(Li0.5Bi0.5) WO4	wolframite	740	27.2	17,000	−56	1.045	0.42	30
(Na0.5Bi0.5)MoO4	scheelite	690	34.4	12,300	+43	1.175	0.41	29
(Na0.5Bi0.5)(Mo0.5W0.5)O4	scheelite	720	28.9	14,000	−6	1.175	0.415	this work
(Na0.5Bi0.5) WO4	scheelite	720	25.7	17,500	−18	1.175	0.42	this work
(Ag0.5Bi0.5)MoO4	scheelite	690	30.4	12,600	+57	1.225	0.41	29
(Ag0.5Bi0.5)(Mo0.5W0.5)O4	scheelite	580	26.3	10,000	+20	1.225	0.415	40
(Ag0.5Bi0.5)WO4	wolframite	580	35.9	13,000	−69	1.225	0.42	41
(K0.5Bi0.5)MoO4	monoclinic	630	37	4,000	+117	1.34	0.41	29

Table 3

Dielectric permittivity, cell volume, calculated and measured molecular polarizability of the (Na0.5Bi0.5)(Mo1−xWx)O4 ceramics.

Composition	εr	Cell volume (Å3)	αmeas (Å3)	αcal (Å3)	Ref.
(Na0.5Bi0.5)MoO4	34.4	322.09/4	17.639	15.28	17
(Na0.5Bi0.5)(Mo0.5W0.5)O4	28.9	322.20/4	17.363	15.24	this work
(Na0.5Bi0.5)WO4	25.7	319.80/4	17.019	15.2	this work

Figure 3

Microwave dielectric permittivities and Qf values of the (Na0.5Bi0.5)(Mo1−xWx)O4 (x = 0, 0.5, 1.0) ceramics as a function of temperature.

Summary

Different from the (Li0.5Bi0.5)(Mo,W)O4 and (Ag0.5Bi0.5)(Mo,W)O4 system, with a ionic radius of 1.18 Å (Na+) between that of Li+ and Ag+, (Na0.5Bi0.5)(Mo,W)O4 system can easily crystallize in standard scheelite structure. Crystal structure refinement based on Rietveld method gave the cell parameters a = b = 5.281 (5) Å, and c = 11.550 (6) Å with a space group I 41/a (88). With increase of W content, microwave permittivity decreased from 34.4 to 25.7 and Qf value increased from 12,300 GHz to 17,500 GHz while TCF shifting from +43 to −18 ppm/°C, which indicates that TCF value is strongly dependent on the [BO4] tetrahedron in scheelite structure. Far-infrared reflectivity further confirmed that phonons at infrared region contributed main dielectric polarization at microwave region. The (Na0.5Bi0.5)(Mo,W)O4 system could be good candidate for Pb-free ULTCC technology.

Methods

summary

The (Na0.5Bi0.5)(Mo1−xWx)O4 (x = 0.0, 0.5 and 1.0) ceramics were prepared via the traditional solid state reaction method as described in our previous work[2, 15]. The calcination temperature is 600 °C and the samples were sintered under air atmosphere in 700~740 °C. XRD was performed using a Rigaku D/MAX-2400 X-ray diffractometry with Cu Kα radiation. The Rietveld profile refinement method was performed on chosen resutls, using Fullprof program[35]. Ceramic surfaces were examined by a FEI Quanta 250 F scanning electron microscopy (SEM). Infrared reflectivity spectra were collected using a Bruker IFS 66 v FTIR spectrometer (on Infrared beamline station (BL01B) at National Synchrotron Radiation Laboratory (NSRL), China). Microwave frequency dielectric properties were obtained using the TE01δ dielectric resonator method[45] with a HP 8720 Network Analyzer and a thermal cycling chamber (Delta 9023, Delta Design, Poway, CA). The temperature coefficient of frequency TCF (τ) was obtained using the following formula:where the f T and f T0 were the TE01δ frequencies at temperature T and T0, respectively.

supplemental information