P E B Wiesse1, Y T Silva-Sousa2, R D Pereira1, C Estrela3, L M Domingues2, J D Pécora1, M D Sousa-Neto1. 1. Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo, Ribeirão Preto, SP, Brazil. 2. Department of Endodontics, Faculty of Dentistry, University of Ribeirão Preto, Ribeirão Preto, SP, Brazil. 3. Department of Stomatological Sciences, Federal University of Goiás, Goiânia, GO, Brazil.
Abstract
AIM: To evaluate the effect of ultrasonic and sonic activation of two root canal sealers on interfacial adaptation and push-out bond strength (BS) to root canal dentine. METHODOLOGY: The root canals of seventy-eight roots of maxillary canines were prepared with NiTi rotary instruments under irrigation with 2.5% NaOCl and 17% EDTA. Canals were filled by lateral condensation of gutta-percha and AH Plus (n = 39) or MTA Fillapex (n = 39). Three subgroups (n = 13) were formed according to sealer activation: no activation (NA), sonic activation (SA, 20 s) and ultrasonic activation (US, 20 s). In three specimens of each subgroup, 0.1% rhodamine B was added to the sealer. Three 1-mm-thick slices were obtained from each root third. The first and second were used for push-out BS test and the third for a qualitative analysis of interfacial adaptation (gaps) and voids by confocal laser scanning microscopy (CLSM). Intratubular penetration of rhodamine B-labelled sealer was also assessed by CLSM. Data were analysed by two-way anova and Tukey's test (α = 0.05). RESULTS: AH Plus (2.58 ± 1.21) had higher push-out BS than MTA Fillapex (1.45 ± 0.71) (P = 0.000). UA (2.64 ± 1.44) had higher BS (P = 0.000) than NA (1.58 ± 0.73) and SA (1.83 ± 0.85), which did not differ significantly from each other (P = 0.3303). The coronal third had higher BS (2.48 ± 1.49) than the middle (2.08 ± 0.94) (P = 0.0003) and apical (1.48 ± 0.58) (P = 0.00) thirds. For both sealers, UA was associated with a more homogeneous filling material with better interfacial adaptation and greater quantity, density and length of tags in dentinal tubules. When UA was used, the tags had similar quantity, density and length to those formed without activation, but interfacial gaps and voids were observed. CONCLUSION: Ultrasonic activation was associated with higher BS values, deeper intratubular penetration and greater interfacial adaptation to root dentine than sonic activation and no activation techniques, AH Plus had higher BS values than MTA Fillapex irrespective of the type of activation.
AIM: To evaluate the effect of ultrasonic and sonic activation of two root canal sealers on interfacial adaptation and push-out bond strength (BS) to root canal dentine. METHODOLOGY: The root canals of seventy-eight roots of maxillary canines were prepared with NiTi rotary instruments under irrigation with 2.5% NaOCl and 17% EDTA. Canals were filled by lateral condensation of gutta-percha and AH Plus (n = 39) or MTA Fillapex (n = 39). Three subgroups (n = 13) were formed according to sealer activation: no activation (NA), sonic activation (SA, 20 s) and ultrasonic activation (US, 20 s). In three specimens of each subgroup, 0.1% rhodamine B was added to the sealer. Three 1-mm-thick slices were obtained from each root third. The first and second were used for push-out BS test and the third for a qualitative analysis of interfacial adaptation (gaps) and voids by confocal laser scanning microscopy (CLSM). Intratubular penetration of rhodamine B-labelled sealer was also assessed by CLSM. Data were analysed by two-way anova and Tukey's test (α = 0.05). RESULTS: AH Plus (2.58 ± 1.21) had higher push-out BS than MTA Fillapex (1.45 ± 0.71) (P = 0.000). UA (2.64 ± 1.44) had higher BS (P = 0.000) than NA (1.58 ± 0.73) and SA (1.83 ± 0.85), which did not differ significantly from each other (P = 0.3303). The coronal third had higher BS (2.48 ± 1.49) than the middle (2.08 ± 0.94) (P = 0.0003) and apical (1.48 ± 0.58) (P = 0.00) thirds. For both sealers, UA was associated with a more homogeneous filling material with better interfacial adaptation and greater quantity, density and length of tags in dentinal tubules. When UA was used, the tags had similar quantity, density and length to those formed without activation, but interfacial gaps and voids were observed. CONCLUSION: Ultrasonic activation was associated with higher BS values, deeper intratubular penetration and greater interfacial adaptation to root dentine than sonic activation and no activation techniques, AH Plus had higher BS values than MTA Fillapex irrespective of the type of activation.
Authors: Bruno Piazza; Melissa Esther Rivera-Peña; Murilo Priori Alcalde; Bruno Carvalho de Vasconcelos; Marco Antonio Húngaro Duarte; Ivaldo Gomes de Moraes; Rodrigo Ricci Vivan Journal: Eur Endod J Date: 2017-12-22