FTIR analysis on aging characteristics of ABS/PC blend under UV-irradiation in air.

Fourier Transform Infrared Spectroscopy (FTIR) is adopted to study the aging characteristics of poly(acrylonitrile-butadiene-styrene)/polycarbonate (ABS/PC) blend under UV-irradiation in air by analyzing the variation of the three main absorbance at about 967cm-1, 1720cm-1 and 3420cm-1 associated with carbon-hydrogen bonds belonging to 1,4 butadiene, carbonyl and hydroxyl groups, respectively. Results indicate that, under UV-irradiation in air, the photo-oxidation of the blend is not a simple combination of the photo-oxidation of corresponding ABS and PC themselves and takes place predominantly at the ABS component. Due to the interaction between the two components and the Fries rearrangement taken place in the PC component during the UV-irradiation in air, the ABS/PC blends behave higher photo-stability than ABS has.