OBJECTIVES: The aim of this study was to investigate the effect of different protocols of 17% ethylene diamine tetra-acetic acid (EDTA) conditioning on the etching pattern and immediate bond strength of universal adhesives to enamel and sclerotic dentin. METHODS AND MATERIALS: Forty bovine teeth with sclerotic dentin and 20 human third molars were randomly divided into eight groups resulting from the combination of the main factors surface treatment (none, two-minute EDTA conditioning manual application, 30-second EDTA manual application, 30-second EDTA sonic application) and adhesives systems (Scotchbond Universal Adhesive [SBU] and Prime & Bond Elect [PBE]). Resin-dentin and enamel-dentin bond specimens were prepared and tested under the microtensile bond strength (μTBS) and microshear bond strength (μSBS) tests, respectively. The etching pattern produced on the unground enamel and the sclerotic dentin surfaces under the different protocols and adhesive systems was evaluated under scanning electron microscopy. RESULTS: For enamel, only the main factor adhesive was significant (p<0.0001), with SBU showing the highest μSBS. In sclerotic dentin, the lowest mean was observed for the group without EDTA application and the highest mean in the group with EDTA application with the sonic device for 30 seconds. Regardless of the EDTA protocol, the highest means of μTBS were observed for SBU (p<0.05). CONCLUSIONS: EDTA conditioning improves the bonding performance of universal adhesives in the self-etch mode on sclerotic dentin, mainly when applied for 30 seconds with the aid of a sonic device. EDTA pretreatment also improves the retentive etching pattern of enamel, but it does not result in higher enamel bond strength.
OBJECTIVES: The aim of this study was to investigate the effect of different protocols of 17% ethylene diamine tetra-acetic acid (EDTA) conditioning on the etching pattern and immediate bond strength of universal adhesives to enamel and sclerotic dentin. METHODS AND MATERIALS: Forty bovine teeth with sclerotic dentin and 20 human third molars were randomly divided into eight groups resulting from the combination of the main factors surface treatment (none, two-minute EDTA conditioning manual application, 30-second EDTA manual application, 30-second EDTA sonic application) and adhesives systems (Scotchbond Universal Adhesive [SBU] and Prime & Bond Elect [PBE]). Resin-dentin and enamel-dentin bond specimens were prepared and tested under the microtensile bond strength (μTBS) and microshear bond strength (μSBS) tests, respectively. The etching pattern produced on the unground enamel and the sclerotic dentin surfaces under the different protocols and adhesive systems was evaluated under scanning electron microscopy. RESULTS: For enamel, only the main factor adhesive was significant (p<0.0001), with SBU showing the highest μSBS. In sclerotic dentin, the lowest mean was observed for the group without EDTA application and the highest mean in the group with EDTA application with the sonic device for 30 seconds. Regardless of the EDTA protocol, the highest means of μTBS were observed for SBU (p<0.05). CONCLUSIONS:EDTA conditioning improves the bonding performance of universal adhesives in the self-etch mode on sclerotic dentin, mainly when applied for 30 seconds with the aid of a sonic device. EDTA pretreatment also improves the retentive etching pattern of enamel, but it does not result in higher enamel bond strength.