Efficacy of silk fibroin-nano silver against Staphylococcus aureus biofilms in a rabbit model of sinusitis.

BACKGROUND: Staphylococcus aureus biofilms contribute significantly to the recalcitrant nature of chronic rhinosinusitis. In previous studies, it has been shown that silk fibroin-nano silver solution can eliminate S. aureus biofilms in vitro, which suggests a potential role of this novel agent in the treatment of biofilm-associated diseases, such as sinusitis.
OBJECTIVE: The aim of this study was to investigate the efficacy of silk fibroin-nano silver solution as a topical anti-biofilm agent in a rabbit model of sinusitis.
METHODS: Biofilm-associated sinusitis models were established in 24 New Zealand White rabbits by gelatin sponge placement and S. aureus inoculation through a hole drilled into the anterolateral wall of the right maxillary sinus. After 4 weeks, indwelling catheters were placed into the maxillary sinus. Different concentrations of silk fibroin-nano silver solution or normal saline were irrigated slowly into the maxillary sinus via the indwelling catheters. After 7 days of irrigation, the rabbits were sacrificed. The sinus mucosa was harvested and examined for biofilm biomass as well as morphological integrity of the epithelium by scanning electron microscopy.
RESULTS: Silk fibroin-nano silver solution was found to be most effective in reducing the biomass of the S. aureus biofilms at a concentration of 384 mg/L, followed by the concentration of 153.6 mg/L, when compared with saline. After treatment with 384 mg/L silk fibroin-nano silver solution, the biofilms were completely eliminated and the injured epithelium was almost restored with regenerated cilia on the surface.
CONCLUSION: Silk fibroin-nano silver solution was found to be an effective topical agent against S. aureus biofilms in the rabbit model of sinusitis, and its effect was concentration-dependent.

Introduction

Bacterial biofilm refers to aggregates of microorganisms embedded in a self-made protective matrix of exopolymers. The bacteria within the biofilms are resistant to antibiotics; in some cases, the resistance may increase a thousand fold.1 Therefore, conventional antibiotic therapy is frequently ineffective in eradicating bacteria in the biofilm. It is generally believed that biofilm is a common cause of persistent infections and chronic inflammatory diseases that are difficult to be cured.2,3

In recent years, biofilms have been consistently detected on the nasal mucosa of patients with chronic rhinosinusitis (CRS).4–11 These are typically associated with more severe disease and with poor outcomes of endoscopic sinus surgery.12,13 Staphylococcus aureus biofilm is increasingly implicated in the pathogenesis of CRS.11,14–16 Evaluation of therapeutic interventions that specifically target S. aureus biofilms in patients with CRS is a key imperative.17,18

Given that the mucosa of the sinus cavities is accessible to topical therapy, it is intuitive to evaluate the effect of topical antibiotics for treatment of biofilm infections. Earlier, the efficacy of silk fibroin–nano silver (SF-NS) solution in disrupting S. aureus biofilms has been demonstrated in vitro.19 This study tested the use of topical SF-NS solution in a rabbit model of S. aureus biofilm-associated sinusitis. The stable existence of S. aureus biofilms on the maxillary sinus mucosa was verified after 4 weeks of bacterial inoculation,20 which gave an opportunity to test this novel therapeutic agent against biofilm under in vivo conditions.

Materials and methods

Animals

Twenty-four New Zealand White rabbits (weight: 2.5–3.5 kg) were obtained from the Laboratory Animal Center at the Fudan University (Shanghai, China). All the experimental protocols were approved by the Animal Care and Use Committee of Fudan University, and the animal study was carried out in accordance with the Ethical Guidelines for Animal Experiments established by Fudan University.

SF-NS solution

The SF-NS solution used in this study was supplied by the State Key Laboratory of Molecular Engineering of Polymers and was made by in situ reduction reaction between natural polymer Bombyx mori silk fibroin and silver nitrate under light. The principles of synthesis of SF-NS and its key characteristics are shown in Figure 1; a more detailed description is available in a previous study.19 The average size of the silver nanoparticle was 12.0±2.1 nm. The minimum bactericidal concentration (MBC) for S. aureus strain (clinical isolate Sa006) was 76.8 mg/L, which was determined according to the Clinical & Laboratory Standards Institute (CLSI, 2011) guidelines for macrodilution in broth.19

Figure 1

Synthesis mechanism and characterization of SF-NS composite.

Notes: (A) Possible mechanism of the reduction of Ag+ ion by tyrosine residues in silk fibroin chain. (B) Transmission electron microscopy images of the synthesized SF-NS particles. (C) High-resolution transmission electron microscopy image of an individual nanoparticle and the electron diffraction pattern. (D) Energy dispersive X-ray spectrum at a single nanocrystal level of the synthesized SF-NS composite.

Abbreviation: SF-NS, silk fibroin–nano silver.

Bacterial preparation

The biofilm-forming Sa006, determined by the traditional crystal violet biofilm assay,21,22 was chosen owing to its relatively strong biofilm formation capacity. The night before the modeling surgery, a single colony of Sa006 was inoculated in tryptic soy broth supplemented with 0.5% glucose (TSBg) and incubated overnight at 37°C with shaking. Then the bacterial suspension was diluted 200-fold with TSBg to achieve a concentration of ~1×106 Colony-Forming Units (CFU)/mL and kept on ice for further use.

Modeling surgery

A rabbit model of S. aureus biofilm-associated sinusitis was established surgically as previously described by our group.20 Briefly, under adequate anesthesia, the skin was incised vertically along the median line of the dorsum. A laterally based flap of periosteum was elevated from the midline to the right side, and then a small hole (diameter: 1.5 mm) was drilled to enter the right maxillary sinus. A piece of compressed absorbable gelatin sponge was inserted into the maxillary sinus, and subsequently inoculated with 0.5 mL of bacterial suspension through the hole. Then, the periosteal and skin incisions were closed with interrupted suture, and the rabbits were caged individually in an air-conditioned room with 12-hour dark–light cycles and free access to water and food.

Indwelling irrigation catheter

Four weeks after modeling surgery, indwelling maxillary sinus irrigation catheters were placed into the right maxillary sinus as described by Chiu et al23 with some modification. Briefly, a plastic catheter connected with an end-enlarged stainless steel needle was used as the irrigating catheter and tunneled under the skin from the vertex to the dorsum incision (Figure 2A). The hub of the metal needle was exposed outside the vertex and secured to the skin with a purse string suture, to avoid its displacement by the animals. The enlarged end of the metal needle under the skin was fixed between the skin and periosteum with interrupted suture to secure the catheter (Figure 2B). Approximately 4 mm of the plastic end was inserted into the maxillary sinus through the hole made in the modeling process (Figure 2C).

Figure 2

Methodology for implantation of indwelling catheter and sinus irrigation.

Notes: (A) A plastic catheter connected with an end-enlarged stainless steel needle (arrow) is being tunneled under the dorsum. (B) The catheter is secured in place by fixation of the enlarged needle end under the skin (*). (C) The plastic end is inserted in the right maxillary sinus. (D) Topical nasal irrigation method.

Abbreviation: SF-NS, silk fibroin–nano silver.

Topical irrigation

The rabbits were randomly divided into four groups (six animals in each group): a blank control group (animal models without irrigation), a negative control group (treated with saline), and two experimental groups (treated with 153.6 and 384 mg/L of SF-NS solution [2× MBC and 5× MBC, respectively]l). The right maxillary sinus was irrigated at a slow pace with test solution, SF-NS solution or normal saline via the indwelling catheter (2 mL twice a day; flow rate: 0.2 mL/s), starting at 1 day after implantation of the indwelling catheter.

Tissue harvest

After 7 days of irrigation, the rabbits were anesthetized with intraperitoneal administration of 10% chloral hydrate (350 mg/kg) and sacrificed with air injection through ear vein. The maxillary sinuses were resected and opened with a pair of scissors. The sinus mucosa was carefully removed, washed thoroughly with saline, and placed in 2.5% glutaraldehyde for scanning electron microscopy (SEM) specimen preparation.

SEM specimen preparation and analysis

The specimens were initially fixed for 24 hours in 2.5% glutaraldehyde at 4°C, then rinsed three times with 1× phosphate-buffered saline (PBS) and fixed with 1% osmium tetroxide for 2 hours. They were then rinsed again three times with PBS, and dehydrated through a graded ethanol series (50%, 70%, 90%, 100%, 15 minutes each). The specimens were then immersed in a mixture of 100% ethanol and isoamyl acetate (2:1), and then in pure isoamyl acetate, for 15 minutes each solution. All specimens were dried in carbon dioxide critical point dryer, sputter coated with gold, and examined with an SU8010 SEM (Hitachi, Tokyo, Japan) at an accelerating voltage of 10 kV. The images were obtained at 2,000× to 5,000× magnification. Structures characterized by water channels, 3D structure, and matrix-embedded spherical bodies were evaluated for evidence of bacterial biofilms.9

For quantitative analysis of biofilm formation on the sinus mucosa in each rabbit, three fields of vision were randomly selected for each specimen. Each field of view (2,000×) was equally divided into nine regions and graded according to the number of biofilm affected regions (average of the three visual fields): lack of involvement of any region was recorded as 0, involvement of 1–3 regions as 1, involvement of 4–6 regions as 2, and involvement of 7–9 regions as 3. Statistical analysis was performed using Kruskal–Wallis rank sum test, and P-value <0.05 was considered as statistically significant.

Results

Overall, the animals tolerated the surgical procedures and catheter implantation well. The irrigation solutions were dripping out of the right nares of all rabbits (Figure 2D). Two of the 24 animals died prematurely during the period of nasal irrigation (one each in the saline group and the 5× MBC group) of pneumonia with empyema, presumably caused by aspiration of the test solutions into the lower respiratory tract. None of the other animals showed signs of systemic illness during the course of the experiment.

The sinuses of the model rabbits in the blank control group were filled with thick mucopurulent secretions, and the mucosa was friable and swollen. The sinuses in the negative control and 153.6 mg/L SF-NS experimental group showed mild to moderate edema of the mucosal linings with mild pus formation. The mucosa in 384 mg/L SF-NS experimental group was very thin and smooth, with no pus in the sinuses.

On SEM, significant differences were observed between specimens from the different groups. For the rabbits without topical irrigation, SEM showed destruction of cilia of the sinus mucosa and clusters of organisms attached to the mucosa with morphological features of biofilms, such as water channels, 3D structure, and matrix-embedded spherical bodies (Figure 3A1 and A2). This phenomenon was observed in all six rabbits in the group. Saline irrigation in the negative control group reduced the bacterial biofilms of the sinus mucosa to a certain extent. However, severe injury of the epithelial layer showed no sign of ciliary regeneration. A considerable portion of the biofilm still existed between the epithelial cells (Figure 3B1 and B2). For the experimental group treated with 153.6 mg/L SF-NS solution, the epithelium was found to have partially repaired with some ciliary buds and short cilia. The biofilms were almost impossible to detect at low magnification (Figure 3C1). However, the cell damage was still visible and a small portion of biofilms still existed; some damaged epithelial cells were observable at high magnification (Figure 3C2). In the experimental group treated with 384 mg/L SF-NS solution, the integrity of the epithelium was almost completely restored with relatively normal cilia; however, some naked epithelial cells were still present, and there was no evidence of bacterial biofilm on the mucosal surface (Figure 3D1 and D2), which was significantly lower than that in the negative control group or 153.6 mg/L of SF-NS-treated experimental group.

Figure 3

Representative scanning electron microscopy images of sinus mucosa from each group.

Notes: (A) Animal model without nasal irrigation. (B–D) Animal models after 7 days of nasal irrigation with (B) normal saline, (C) SF-NS solution (153.6 mg/L), and (D) SF-NS solution (384 mg/L) (A1–D1, 2,000×; A2–D2, 5,000×).

Abbreviation: SF-NS, silk fibroin–nano silver.

Quantitative analysis of bacterial biofilm revealed statistically significant between-group differences (Table 1). Although the bacterial biofilms on the sinus mucosa of the negative control group were reduced to a certain extent, statistical analysis showed that there was no significant difference in the range of biofilm involvement when compared with that in the blank control group. Although the bacterial biofilm involvement in the 153.6 mg/L SF-NS experimental group was significantly lower than that in blank control group, no significant difference was observed when compared with the saline group. However, the 384 mg/L SF-NS group showed the least biofilm involvement; the between-group difference with each of the other three groups was statistically significant.

Table 1

Comparison of bacterial biofilm involvement in each group

Level	No in each group				Total	Rank range	Average Rank	Rank of each group
	A	B	C	D				A	B	C	D
0	0	0	0	4	4	1–4	2.5	0	0	0	10
1	0	0	4	1	5	5–9	7	0	0	28	7
2	4	4	2	0	10	10–19	14.5	58	58	29	0
3	2	1	0	0	3	20–22	21	42	21	0	0
Total	6	5	6	5				100	79	57	17

Notes: Group A, blank control group; Group B, negative control group treated with saline; Group C, experimental group treated with 153.6 mg/L SF-NS solution; Group D, experimental group treated with 384 mg/L SF-NS solution.

Abbreviations: No, number; SF-NS, silk fibroin–nano silver.

Discussion

Topical nasal irrigation has been used for thousands of years for nasal health. The obvious advantage of topical administration is the higher local concentration of the therapeutic agent with minimal systemic side effects. In recent years, management of biofilm-associated CRS has largely been confined to topical administration of antimicrobials.24–27 This study evaluated the efficacy of SF-NS solution as a topical anti-biofilm agent in a rabbit model of sinusitis. The results showed that topical nasal irrigation, even with saline, has certain benefits in decreasing the biomass of the S. aureus biofilm in the sinuses of the rabbits.

However, although the saline irrigation is beneficial in reducing the microorganisms attached to the mucosal surface, yet a significant portion of the biofilms still persisted between the epithelial cells along with severe epithelial injury. This suggests that the saline might just remove the superficial and loose structure of the biofilms. This could be attributed to the lack of nutrients in the superficial layers of the biofilm, which results in fall off of the dead or dormant microorganisms. However, the viable biofilms located in deep sites or between the epithelial cells, which directly damaged the epithelium, were not eliminated by saline irrigation alone.

In vitro experiments found that SF-NS solution at 2× MBC level destroyed S. aureus biofilms partially, and when the concentration increased to 5× MBC, the biofilms were totally destroyed.19 Although in vitro and in vivo conditions are not the same, yet the purpose is the same, which is to observe biofilm-disrupting properties of SF-NS after direct contact with the biofilms. Hence, SF-NS solution was used at the concentrations of 153.6 and 384 mg/L (2× MBC and 5× MBC, respectively) as anti-biofilm agents in this study. Results showed that SF-NS solution at 2× MBC level is more effective in reducing the biofilm biomass when compared with saline. Although a small amount of biofilm still existed in some damaged epithelial cells, the injured epithelium exhibited signs of restoration, which indicated that it was the SF-NS component of the solution which acted against the biofilm and that the biofilm was not removed solely by the flushing action. This suggested that better results may be achieved if the duration of treatment is further extended.

Topical application of SF-NS solution at the 5× MBC level eliminated S. aureus biofilms in the sinuses of the rabbits after irrigation for 7 days. Furthermore, the integrity of epithelium had been recovered and most of the epithelial cells were normal with regeneration of cilia, which indicates that the repair of the epithelial cells had been in progress for some time.

The association of ciliary beat defect with CRS is well acknowledged. As noted in the experiment, a marked destruction of the sinonasal epithelium was observed with a complete absence of cilia, when the sinonasal mucosa was colonized by bacterial biofilms. Thus, as stated by Galli et al, biofilm formation represents the later phase of the inflammatory process that leads to complete epithelial destruction.28 The results of the present study clearly showed restoration of epithelium and cilia after treatment with SF-NS solutions. This can easily be considered as the consequence of biofilm removal by silver nanoparticles. Thus, although the mechanism of nasal epithelial restoration is still poorly understood, treatment of bacterial biofilms may be a key factor for ciliary recovery in biofilm-affected nasal mucosa. Although studies have found that silk fibroin has a role in promoting reepithelialization,29,30 the role of silk fibroin in epithelial restoration in this severe inflammatory condition needs to be studied further.

The antibacterial property of silver nanoparticles against a broad spectrum of bacteria has been increasingly used in various fields.31 Nonetheless, individual silver nanoparticles are easily oxidized and/or aggregated in air, which hampers their practical application.32 This study used green product SF-NS synthesized by the reaction of silk fibroin and silver nitrate, detailed information on which can be found in our previously published literature.19 The silk fibroin acted as a soluble template for biomineralization and the tyrosine residues in the silk fibroin backbone were thought to be responsible for the reduction of Ag+ into silver nanoparticles in situ. Silk fibroin is a natural nonionic surfactant that enhances the stability of silver nanoparticles in aqueous dispersion.33 Therefore, silk fibroin acts simultaneously as a reducing, dispersing, and stabilizing agent of the synthesized silver nanoparticles. In a previous study,19 it was found that synthesized SF-NS retained the antimicrobial properties of silver nanoparticles and could dissolve in water without aggregation, which makes it suitable for use as a solution for treatment. This study demonstrated that SF-NS solution is effective against mature biofilms formed by S. aureus in vivo in a concentration-dependent manner. Although 2× MBC and 5× MBC levels of SF-NS solutions showed no negative impact on the morphology of epithelial cells and cilia, for clinical use the other characteristics of silver nanoparticles still need to be considered, such as whether they can be easily taken up in the cells, and their potential toxic effects. Further studies will be carried out in the future to establish these facts.

Conclusion

SF-NS solution at concentrations of 153.6 and 384 mg/L was found to be an effective topical nasal antimicrobial agent, which reduced the biomass of S. aureus biofilms in the rabbit model of sinusitis. The clinical utility of SF-NS solution for patients with biofilm-associated CRS is yet to be determined. However, the anti-biofilm properties of SF-NS solution provide another option for future therapeutic interventions for biofilm-associated sinusitis.