Kenichi Oe1, Hirokazu Iida2, Narumi Ueda2, Tomohisa Nakamura2, Naofumi Okamoto2, Yusuke Ueda2. 1. Department of Orthopaedic Surgery, Kansai Medical University, 2-5-1 Shinmachi, Hirakata, Osaka 573-1010, Japan. Electronic address: oeken@hirakata.kmu.ac.jp. 2. Department of Orthopaedic Surgery, Kansai Medical University, 2-5-1 Shinmachi, Hirakata, Osaka 573-1010, Japan.
Abstract
BACKGROUND: Although antibiotic-loaded acrylic cement (ALAC) is used to prevent and treat periprosthetic hip infection, it is unknown how much antibiotic is deposited in the body in vivo, how high the serum concentration rises, or how long its effects last. The aim of this study was firstly to determine the amount of vancomycin (VCM) deposited as ALAC in the body, and secondly to assess the safety and drug elution profile of VCM in ALAC. METHODS: We administered VCM to prevent infection after total hip arthroplasty (THA) or to treat patients with methicillin-resistant Staphylococcus aureus. Patients were classified into two groups: a low-dose group (21 hips) that received primary THA for high-risk cases, revision THA without infection, or one-staged revision THA for infection; and a high-dose group (6 hips) that received cement beads during a two-staged revision THA. The amount of VCM placed as ALAC into the hip was calculated using the remaining ALAC. The serum concentrations of VCM and creatinine were evaluated at postoperative days 1, 4, 7, 14, and 28, and at 3 and 6 months. RESULTS: The mean amount of VCM placed as ALAC into the hip was 0.9 g and 3.4 g for cemented THA and cement beads, respectively (P < 0.0001). The mean serum concentration of VCM from ALAC in the high-dose group was significantly increased compared with that in the low-dose group on postoperative days 1, 4, 7, 14, and 28 (P < 0.0001), but it remained within a clinically safe range. No significant differences were observed between the preoperative and postoperative serum creatinine levels of either group. CONCLUSION: The average serum concentrations of VCM from ALAC were always less than the effective blood concentration, and were detectable until 6 months after surgery.
BACKGROUND: Although antibiotic-loaded acrylic cement (ALAC) is used to prevent and treat periprosthetic hip infection, it is unknown how much antibiotic is deposited in the body in vivo, how high the serum concentration rises, or how long its effects last. The aim of this study was firstly to determine the amount of vancomycin (VCM) deposited as ALAC in the body, and secondly to assess the safety and drug elution profile of VCM in ALAC. METHODS: We administered VCM to prevent infection after total hip arthroplasty (THA) or to treat patients with methicillin-resistant Staphylococcus aureus. Patients were classified into two groups: a low-dose group (21 hips) that received primary THA for high-risk cases, revision THA without infection, or one-staged revision THA for infection; and a high-dose group (6 hips) that received cement beads during a two-staged revision THA. The amount of VCM placed as ALAC into the hip was calculated using the remaining ALAC. The serum concentrations of VCM and creatinine were evaluated at postoperative days 1, 4, 7, 14, and 28, and at 3 and 6 months. RESULTS: The mean amount of VCM placed as ALAC into the hip was 0.9 g and 3.4 g for cemented THA and cement beads, respectively (P < 0.0001). The mean serum concentration of VCM from ALAC in the high-dose group was significantly increased compared with that in the low-dose group on postoperative days 1, 4, 7, 14, and 28 (P < 0.0001), but it remained within a clinically safe range. No significant differences were observed between the preoperative and postoperative serum creatinine levels of either group. CONCLUSION: The average serum concentrations of VCM from ALAC were always less than the effective blood concentration, and were detectable until 6 months after surgery.