Adsorption performance of salicylic acid on a novel resin with distinctive double pore structure.

Two approaches were used to synthesize two resins with different pore structures. In one way, the CH2Cl groups in macroporous chloromethylated polystyrene resin were transformed to methylene bridges, and achieved a hypercrosslinked resin with plentiful micropores (denoted GQ-06). In the other way, 50% of the CH2Cl groups in chloromethylated polystyrene resin was used to produce micropores, while the residual 50% of the CH2Cl groups was reacted with 2-aminopyridine, and prepared another resin with double pore structure of hypercrosslinked resin and macroporous resin (denoted GQ-11). The adsorption of salicylic acid (SA) on GQ-11 was investigated using GQ-06 as the reference adsorbent. The effect of pH on the adsorption of SA on GQ-06 was consistent with the dissociation curve of SA. The maximum adsorption capacity of SA on GQ-11 was observed at the solution pH of 2.64. The greater adsorption rate of SA on GQ-11 than that of GQ-06 was attributed to its double pore structure. The multifunctional adsorption mechanism of anion exchange and hydrophobic interaction resulted in the larger equilibrium capacity of SA on GQ-11 than that of GQ-06. GQ-06 and GQ-11 could be regenerated by absolute alcohol and 80% of alcohol -0.5mol/L of sodium hydroxide aqueous solution, respectively.