OBJECTIVE: The objective of the present study was to assess the effect of erbium, chromium: yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser-activated irrigation (LAI) of NaOCl on the push-out bond strength of furcal perforations repaired with ProRoot mineral trioxide aggregate (MTA) and Biodentine. BACKGROUND DATA: Several studies investigated the adhesion of calcium silicate-based cements after exposure to endodontic irrigants, while effect of LAI on bond strength remains to be elucidated. MATERIALS AND METHODS: Bur-cut furcal perforations with standard dimensions were created in 100 extracted human mandibular molars. Teeth were randomly distributed into two groups (n = 50/group) according to the repair material applied: (1) ProRoot MTA or (2) Biodentine. The specimens were further assigned into five subgroups according to the irrigation regimens used over the set materials: (a) distilled water with needle irrigation; (b) 5.25% NaOCl with needle irrigation; (c) distilled water with LAI; (d) 5.25% NaOCl with LAI; and (e) no irrigation (control). Bond strengths of the test materials were assessed by using push-out bond strength test. RESULTS: Biodentine showed significantly higher dislocation resistance than ProRoot MTA (p < 0.05). Laser activation of 5.25% NaOCl and distilled water did not significantly affect the push-out bond strength results (p > 0.05). CONCLUSIONS: Biodentine showed higher dislocation resistance than ProRoot MTA as a perforation repair material. Er,Cr:YSGG laser activation of irrigation aqueous solutions had no adverse effect on push-out bond strength of Biodentine and ProRoot MTA.
OBJECTIVE: The objective of the present study was to assess the effect of erbium, chromium: yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser-activated irrigation (LAI) of NaOCl on the push-out bond strength of furcal perforations repaired with ProRoot mineral trioxide aggregate (MTA) and Biodentine. BACKGROUND DATA: Several studies investigated the adhesion of calcium silicate-based cements after exposure to endodontic irrigants, while effect of LAI on bond strength remains to be elucidated. MATERIALS AND METHODS: Bur-cut furcal perforations with standard dimensions were created in 100 extracted human mandibular molars. Teeth were randomly distributed into two groups (n = 50/group) according to the repair material applied: (1) ProRoot MTA or (2) Biodentine. The specimens were further assigned into five subgroups according to the irrigation regimens used over the set materials: (a) distilled water with needle irrigation; (b) 5.25% NaOCl with needle irrigation; (c) distilled water with LAI; (d) 5.25% NaOCl with LAI; and (e) no irrigation (control). Bond strengths of the test materials were assessed by using push-out bond strength test. RESULTS:Biodentine showed significantly higher dislocation resistance than ProRoot MTA (p < 0.05). Laser activation of 5.25% NaOCl and distilled water did not significantly affect the push-out bond strength results (p > 0.05). CONCLUSIONS:Biodentine showed higher dislocation resistance than ProRoot MTA as a perforation repair material. Er,Cr:YSGG laser activation of irrigation aqueous solutions had no adverse effect on push-out bond strength of Biodentine and ProRoot MTA.
Authors: Andrea Cardoso Pereira; Mariana Valerio Pallone; Marina Angélica Marciano; Karine Laura Cortellazzi; Marcos Frozoni; Brenda P F A Gomes; José Flávio Affonso de Almeida; Adriana de Jesus Soares Journal: Restor Dent Endod Date: 2019-05-09
Authors: Elena Rebolloso de Barrio; Juan José Pérez-Higueras; Ernesto García-Barbero; Lucía Gancedo-Caravia Journal: BMC Oral Health Date: 2021-11-19 Impact factor: 2.757