Biomechanics of Polyhydroxyalkanoate Mesh-Augmented Single-Row Rotator Cuff Repairs.

Polyhydroxyalkanoate (PHA) mesh is a bioresorbable scaffold used to reinforce the suture-tendon interface in rotator cuff repairs (RCRs). We conducted a study of cyclic and ultimate failure properties of PHA mesh-augmented single-row RCRs and nonaugmented RCRs. Eight pairs of fresh-frozen cadaver humeri (6 male, 2 female) were tested. Mean (SD) age was 61 (9) years. The supraspinatus tendon was resected and reattached in a single-row configuration using 2 triple-loaded suture anchors and 6 simple stitches. The opposite humerus underwent RCR augmented with 2 strips of 13-mm × 23-mm PHA mesh. Humeri were mounted in an Instron load frame, cycled 1000 times to 1.0 MPa of effective stress, and loaded to failure. Construct gapping and ultimate failure loads/displacements were recorded. Paired t tests compared augmented and nonaugmented RCRs (P ≤ .05 was significant). There was no difference in gapping over 1000 cycles (P = .879). Mean (SD) failure load was higher for PHA mesh-augmented RCRs, 571 (173) N, than for nonaugmented (control) RCRs, 472 (120) N (P = .042), and failures were consistent within pairs because of tissue failure at the knots or anchor pullout. This technique for arthroscopic augmentation can be used to improve initial biomechanical repair strength in tears at risk for failure.